Micro-mechanisms of rate dependent tensile deformation for LY12 aluminium alloy

被引:0
|
作者
Wu Yanqing [1 ]
机构
[1] Beijing Inst Technol, State Key Lab Explos Sci & Technol, Beijing 100081, Peoples R China
关键词
LY12; alloy; strain rate dependence deformation; precipitation phase; substructure;
D O I
暂无
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The great change of LY12 alloy property took place after the alloy underwent high temperature and low strain rates (elongation up to 17%) followed by room-temperature tension. It was found that the flow stress of LY12 aluminum alloy reduced to only ten percent of the yield point after undergoing high-temperature deformation at low strain rate (10-4 s(-1)), and the elongation to fracture increased by one time. This abnormal room-temperature property strongly depends on the tensile strain rates and temperature and the cooling rate. By comparison, the sample subjected to high-temperature deformation at higher strain rate (10(-1) s(-1)) showed brittle-like behavior after cooled up to room temperature, i.e. a sudden increase in flow stress and rupture quickly. From the point view of precipitate and substructures, the characteristics of microstructure are described by TEM analyses. Combined with SEM fracture surface analysis, the corresponding fracture mode and mechanisms are expatiated.
引用
收藏
页码:2109 / 2113
页数:5
相关论文
共 12 条
  • [1] Coexistence of clusters, GPB zones, S"-, S′- and S-phases in an Al-0.9% Cu-1.4% Mg alloy
    Charai, A
    Walther, T
    Alfonso, C
    Zahra, AM
    Zahra, CY
    [J]. ACTA MATERIALIA, 2000, 48 (10) : 2751 - 2764
  • [2] INFLUENCES OF MATERIAL PARAMETERS AND MICROSTRUCTURE ON SUPERPLASTIC FORMING
    GHOSH, AK
    HAMILTON, CH
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (05): : 733 - 743
  • [3] TENSILE INSTABILITY AND NECKING IN MATERIALS WITH STRAIN-HARDENING AND STRAIN-RATE HARDENING
    GHOSH, AK
    [J]. ACTA METALLURGICA, 1977, 25 (12): : 1413 - 1424
  • [4] MICROSTRUCTURAL EVOLUTION BY CONTINUOUS RECRYSTALLIZATION IN A SUPERPLASTIC AL-MG ALLOY
    HALES, SJ
    MCNELLEY, TR
    [J]. ACTA METALLURGICA, 1988, 36 (05): : 1229 - 1239
  • [5] Effects of preferentially aligned precipitates on plastic anisotropy in Al-Cu-Mg-Ag and Al-Cu alloys
    Hargarter, H
    Lyttle, MT
    Starke, EA
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 257 (01): : 87 - 99
  • [6] HATCH JE, 1984, ALUMINUM PROPERTIES, P139
  • [7] Superplastic-like behavior in medium grained and single crystalline Al-Mg solid solution alloys
    Ito, T
    Shibasaki, S
    Koma, M
    Otsuka, M
    [J]. JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2002, 66 (04) : 409 - 417
  • [8] Flow behavior and microstructures of large-grained Fe3Si during high temperature deformation
    Kim, WY
    Hanada, S
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2002, 347 (1-2) : 219 - 227
  • [9] Tensile deformation behavior of aluminum alloys at warm forming temperatures
    Li, DM
    Ghosh, A
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 352 (1-2): : 279 - 286
  • [10] The role of dislocations in high-strain-rate superplasticity of an Al-Ni-misch metal alloy
    Umakoshi, Y
    Fujitani, W
    Nakano, T
    Inoue, A
    Ohtera, K
    Mukai, T
    Higashi, K
    [J]. ACTA MATERIALIA, 1998, 46 (13) : 4469 - 4478