Effect of internal stress on the electro-optical behaviour of Al-doped ZnO transparent conductive thin films

In this work, we will report on scientific efforts aimed at unraveling the quantitative effect of elastic strain on the electro-optical behaviour of Al-doped zinc oxide (AZO). AZO thin films have been deposited by reactive magnetron sputtering to thicknesses from 300 to 500 nm, both on extra-clear glass substrates as well as on oxidised Si wafers. This resulted in both cases in polycrystalline, strongly textured (002) films. During deposition, the internal stress evolution in the growing film was monitored in-situ using high resolution curvature measurements. The resulting growth-induced elastic strain, which was found to depend heavily on the oxygen partial pressure, could further be modulated by appropriately choosing the deposition temperature. The latter also induces an additional extrinsic thermal stress component, whose sign depends on the substrate used. As such, a wide range of biaxial internal stresses could be achieved, from 600MPa in compression up to 800MPa in tension. The resulting charge carrier mobilities, obtained independently from room temperature Hall measurements, were found to range between 5 and 25 cm(2)/V s. Interestingly, the maximum mobility occurred at the zero-stress condition, and together with a charge carrier concentration of about 8 x 10(20) cm(-3), this gave rise to a resistivity of only 300 mu Omega cm. From the stress-dependent optical transmission spectra in the range of 200-1000 nm, the pressure coefficient of the optical bandgap was estimated from the corresponding Tauc plots to be 31meV/GPa, indicating a very high strain-sensitivity as well. Published by AIP Publishing.