Grain growth kinetics and the effect of crystallographic anisotropy on normal grain growth of quartz

Annealing experiments on agate were performed to investigate grain growth kinetics and the effect of crystallographic anisotropy on normal grain growth of quartz. The experiments were conducted using a piston-cylinder apparatus at 700-800A degrees C and 0.5 GPa for 0-66 h. The grain growth rate was expressed by D (n) -D (0) (n) = kt with k = k (0) exp(-H*/RT) where D (0) is the initial grain size at t = 0, with n = 4.4 +/- A 0.3, and H* = 191.3 +/- A 11.0 kJ/mol is the activation enthalpy and logk (0) = 19.8 +/- A 1.4. While the grain aspect ratios are nearly constant at similar to 0.7 (short/long) during grain growth, the longest axis in individual grains tends to be oriented parallel to their c-axis, indicating that a primary crystal-preferred orientation of c-axis of the agate could result in the development of a weak shape-preferred orientation during grain growth.