Hydriding behavior of spherical particles of a titanium-aluminum-tin alloy

被引：1
|
作者：
Fokin, VN [1 ]
Fokina, EE [1 ]
Torbov, VI [1 ]
Tarasov, BP [1 ]
Shilkin, SP [1 ]
Andrievskii, RA [1 ]
机构：
[1] Russian Acad Sci, Inst Problems Chem Phys, Chernogolovka 142432, Moscow Oblast, Russia
来源：
INORGANIC MATERIALS | 2006年 / 42卷 / 03期
基金：
俄罗斯基础研究基金会;
关键词：
Hydrogen; Titanium; Inorganic Chemistry; Thermal Stability; Hydride;
D O I：
10.1134/S0020168506030095
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The hydriding behavior of the VT5-1 alloy (92.05 wt % Ti + 4.52 wt % Al + 3.43 wt % Sn) in the form of spherical particles 0.1, 0.4, 0.6, and 0.8 mm in diameter was studied at temperatures from 820 to 973 K and hydrogen pressures from 1 to 6 MPa. The results indicate that the absorption capacity of VT5-1 is lower than that of titanium and that the thermal stability of the resultant mixed-metal hydride is lower than that of titanium dihydride.
引用
收藏
页码：261 / 263
页数：3
相关论文
共 50 条
  • [1] Hydriding behavior of spherical particles of a titanium-aluminum-tin alloy
    V. N. Fokin
    E. E. Fokina
    V. I. Torbov
    B. P. Tarasov
    S. P. Shilkin
    R. A. Andrievskii
    Inorganic Materials, 2006, 42 : 261 - 263
  • [2] INFLUENCE OF TIN AND ALUMINUM ON THE TRANSITION BEHAVIOR OF OXYGENATED TITANIUM
    RENNHACK, EH
    LIBSCH, JF
    TRANSACTIONS OF THE AMERICAN INSTITUTE OF MINING AND METALLURGICAL ENGINEERS, 1959, 215 (06): : 942 - &
  • [3] Surface Characteristics of Plasma Treated and Titanium Nitride (TiN) Deposited Aluminum Alloy
    Balanand, Santhosh
    Bhowmik, Shantanu
    Datta, Madhav
    Rane, Ramkrishna
    Mukherjee, Subrato
    MATERIALS PERFORMANCE AND CHARACTERIZATION, 2019, 8 (01)
  • [4] Behavior of magnesium and tin at the surface of aluminum-silicon-magnesium-tin alloy powder particles at elevated temperature and their effect on direct nitriding reaction
    Kondoh, K
    Kimura, A
    Takeda, Y
    Watanabe, R
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2000, 64 (11) : 1106 - 1112
  • [5] Chemical behavior of titanium in a liquid aluminum-silicon alloy
    Peronnet, M
    Barbeau, F
    Bosselet, F
    Viala, JC
    Bouix, J
    JOURNAL DE PHYSIQUE IV, 1999, 9 (P4): : 223 - 228
  • [6] Microstructure and mechanical property of brazed joints in titanium alloy and aluminum alloy combination with tin foil interlayer
    Xinjian Yuan
    Xuebo Liang
    Xiuyang Li
    Miao Hong
    Kunlun Tang
    International Journal of Precision Engineering and Manufacturing, 2015, 16 : 1293 - 1297
  • [7] Microstructure and Mechanical Property of Brazed Joints in Titanium Alloy and Aluminum Alloy Combination with Tin Foil Interlayer
    Yuan, Xinjian
    Liang, Xuebo
    Li, Xiuyang
    Hong, Miao
    Tang, Kunlun
    INTERNATIONAL JOURNAL OF PRECISION ENGINEERING AND MANUFACTURING, 2015, 16 (07) : 1293 - 1297
  • [8] Evaporation Behavior of Aluminum from Titanium Alloy Melt with Different Initial Aluminum Contents
    Mizukami, Hideo
    Shirai, Yoshihisa
    Mitchell, Alec
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2022, 108 (07): : 383 - 393
  • [9] Evaporation Behavior of Aluminum from Titanium Alloy Melt with Different Initial Aluminum Contents
    Mizukami, Hideo
    Shirai, Yoshihisa
    Mitchell, Alec
    ISIJ INTERNATIONAL, 2022, 62 (06) : 1106 - 1115
  • [10] HYDRIDING BEHAVIOR OF COMPOSITE-MATERIAL CONSISTING OF ULTRAFINE METAL PARTICLES AND HYDROGEN-STORAGE ALLOY
    UEMURA, Y
    KARASUMARU, R
    HATATE, Y
    KAGAKU KOGAKU RONBUNSHU, 1992, 18 (03) : 322 - 329
12345