Microstructure and Hardness of T250 Maraging Steel in Heat Affected Zone

被引:11
|
作者
Mo De-feng [1 ]
Hu Zheng-fei [1 ]
Chen Shu-juan [1 ]
Wang Chun-xu [2 ]
He Guo-qiu [1 ]
机构
[1] Tongji Univ, Sch Mat Sci & Engn, Shanghai 200092, Peoples R China
[2] Cent Iron & Steel Res Inst, Beijing 100081, Peoples R China
基金
中国国家自然科学基金;
关键词
T250 maraging steel; electron-beam weld; microstructure; microhardness;
D O I
10.1016/S1006-706X(09)60016-9
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Electron-beam (EB) welding was used in T250 maraging steel, microstructures of both base material and heat affected zone (HAZ) were investigated by optical microscopy (OM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM), and microhardness was tested. The results showed that during EB welding, the HAZ of T250 maraging steel exhibited a continuous gradient structure. The microstructure of the entire HAZ, from fusion line, could be divided into four zones: fusion zone, overheated zone, transition zone, and hardened zone. The microhardness showed a distinct regularity in each area. The softest region was the fusion zone, whereas the hardest was the hardened zone. In the overheated zone, the hardness increased as the grain size decreased. Furthermore, in the transition zone, the hardness level dropped noticeably. The peak temperature during the thermal cycle had a great influence on the formation of reverted austenite and dissolution of the precipitated particles, which contributed a lot to the microstructure and hardness of this material.
引用
收藏
页码:87 / 91
页数:5
相关论文
共 50 条
  • [1] Microstructure and Hardness of T250 Maraging Steel in Heat Affected Zone
    De-feng Mo
    Zheng-fei Hu
    Shu-juan Chen
    Chun-xu Wang
    Guo-qiu He
    Journal of Iron and Steel Research International, 2009, 16 : 87 - 91
  • [2] Microstructure and Hardness of T250 Maraging Steel in Heat Affected Zone
    MO De-feng~1 HU Zheng-fei~1 CHEN Shu-juan~1 WANG Chun-xu~2 HE Guo-qiu~1 1.School of Material Science and Engineering
    2.Central Iron and Steel Research Institute
    JournalofIronandSteelResearch(International), 2009, 16 (01) : 87 - 91
  • [3] Effect of Tube Spinning With Subsequent Heat-Treatment on Performance and Microstructure Evolution of T250 Maraging Steel
    Hu Zheng-fei
    Wang Chun-xu
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2012, 19 (05) : 63 - 68
  • [4] Effect of Tube Spinning With Subsequent Heat-Treatment on Performance and Microstructure Evolution of T250 Maraging Steel
    HU Zheng-fei1
    2. China Iron and Steel Institute Group
    JournalofIronandSteelResearch(International), 2012, 19 (05) : 63 - 68
  • [5] Effect of Tube Spinning With Subsequent Heat-Treatment on Performance and Microstructure Evolution of T250 Maraging Steel
    Zheng-fei Hu
    Chun-xu Wang
    Journal of Iron and Steel Research International, 2012, 19 : 63 - 68
  • [6] Microstructure, Performance and Phase Study on T250 Maraging aging steel Pipe after Spinning and Aging
    Chen, Caihong
    Zhang, Shaoyu
    Min, Yong'an
    PROCEEDINGS OF THE 2015 INTERNATIONAL CONFERENCE ON ADVANCED ENGINEERING MATERIALS AND TECHNOLOGY, 2015, 38 : 881 - 886
  • [7] STRENGTH AND TOUGHNESS OF T250 MARAGING STEEL JOINT HYBRID-TREATED WITH LASER WELDING AND AGING
    Li Kun
    Shan Jiguo
    Wang Chunxu
    Tian Zhiling
    ACTA METALLURGICA SINICA, 2015, 51 (08) : 904 - 912
  • [8] Hardness testing in the heat affected zone of steel weld
    Anon
    Indian Welding Journal, 1988, 20 (03): : 381 - 386
  • [9] Prediction of hardness distribution in steel heat affected zone
    Kasuya, T
    Hashiba, Y
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 1999, 4 (05) : 265 - 275
  • [10] PREDICTION OF MICROSTRUCTURE AND HARDNESS OF MULTIPASS HEAT AFFECTED ZONE IN HIGH STRENGTH STEEL GIRTH WELDS
    Di Nunzio, Paolo Emilio
    Cesile, Maria Cristina
    Anelli, Ettore
    Richard, Gilles
    NEW DEVELOPMENTS ON METALLURGY AND APPLICATIONS OF HIGH STRENGTH STEELS: BUENOS AIRES 2008, VOLS 1 AND 2, PROCEEDINGS,, 2008, : 597 - +