Comparative analysis of structure and phase composition for alloys 45Kh26N33S2B2 and 45X25H20C2 after long-term exposure to high temperatures and static load

被引：0
|
作者：
Oryshchenko, A. S.
Nesterova, E. V.
Utkin, Yu. A.
机构：
[1] Prometei Central Research Institute for Structural Materials, St. Petersburg
来源：
METALLURGIST | 2008年 / 52卷 / 3-4期
关键词：
Alloys;
D O I：
10.1007/s11015-008-9029-8
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Electron microscopy was used to determine the nature of the structural changes in 45Kh26N33S2B2 alloy, and the nature and chemical composition of proeutetoid constituents, based on tests of samples of this material for long-term strength at high temperature.
引用
收藏
页码：182 / 191
页数：10
相关论文
共 9 条
  • [1] Comparative analysis of structure and phase composition for alloys 45Kh26N33S2B2 and 45X25H20C2 after long-term exposure to high temperatures and static load
    A. S. Oryshchenko
    E. V. Nesterova
    Yu. A. Utkin
    Metallurgist, 2008, 52 : 182 - 191
  • [2] Special Features of Structure and Long-Term Strength of Cast Refractory Alloy 45Kh26N33S2B2
    A. I. Rudskoy
    A. S. Oryshchenko
    S. Yu. Kondrat’ev
    G. P. Anastasiadi
    M. D. Fuks
    S. N. Petrov
    Metal Science and Heat Treatment, 2013, 55 : 209 - 215
  • [3] Special Features of Structure and Long-Term Strength of Cast Refractory Alloy 45Kh26N33S2B2
    Rudskoy, A. I.
    Oryshchenko, A. S.
    Kondrat'ev, S. Yu.
    Anastasiadi, G. P.
    Fuks, M. D.
    Petrov, S. N.
    METAL SCIENCE AND HEAT TREATMENT, 2013, 55 (3-4) : 209 - 215
  • [4] Mechanism and Kinetics of Phase Transformations in Refractory Alloy 45Kh26N33S2B2 Under Long-Term High-Temperature Holds. Part 2
    A. I. Rudskoy
    S. Yu. Kondrat’ev
    G. P. Anastasiadi
    A. S. Oryshchenko
    M. D. Fuks
    Metal Science and Heat Treatment, 2014, 56 : 124 - 130
  • [5] Mechanism and Kinetics of Phase Transformations in Refractory Alloy 45Kh26N33S2B2 Under Long-Term High-Temperature Holds. Part 2
    Rudskoy, A. I.
    Kondrat'ev, S. Yu.
    Anastasiadi, G. P.
    Oryshchenko, A. S.
    Fuks, M. D.
    METAL SCIENCE AND HEAT TREATMENT, 2014, 56 (3-4) : 124 - 130
  • [6] Mechanisms and Kinetics of Phase Transformations in Refractory Alloy 45Kh26N33S2B2 in Long-Term High-Temperature Holds. Part 1
    A. I. Rudskoy
    A. S. Oryshchenko
    S. Yu. Kondrat’ev
    G. P. Anastasiadi
    M. D. Fuks
    Metal Science and Heat Treatment, 2014, 56 : 3 - 8
  • [7] Mechanisms and Kinetics of Phase Transformations in Refractory Alloy 45Kh26N33S2B2 in Long-Term High-Temperature Holds. Part 1
    Rudskoy, A. I.
    Oryshchenko, A. S.
    Kondrat'ev, S. Yu.
    Anastasiadi, G. P.
    Fuks, M. D.
    METAL SCIENCE AND HEAT TREATMENT, 2014, 56 (1-2) : 3 - 8
  • [8] Investigation of transformations of structure, phase composition, and mechanical properties of 45Cr26Ni33Si2Nb2 alloy during high-temperature test for long-term strength of metal of a centrifugal casting pipe
    Oryshchenko A.S.
    Utkin Yu.A.
    Petrov S.N.
    Nesterova E.V.
    Mikhailov-Smol'Nyakov M.S.
    Inorganic Materials: Applied Research, 2013, 4 (6) : 494 - 501
  • [9] Crystal structure of 3,6,9,12,20,23,26,29-octaoxa-36,49-dithia-51,52-diaza-hexacyclo[16.16.16.138,42.143,47.014,50.031,35]dopentaconta-1(35),14,16,18(50),31,33,38,40,42(52),43,45,47(51)-dodecaene, C40H48N2O8S2, a 2,2′-bipyridine-bridged macrocyclic polyether
    Nabeshima, T
    Horn, E
    Aoki, T
    Yano, Y
    ZEITSCHRIFT FUR KRISTALLOGRAPHIE-NEW CRYSTAL STRUCTURES, 2000, 215 (01): : 19 - 20
1