Synthesis and electrochemical performance of LiNi0.7Co0.15Mn0.15O2 as gradient cathode material for lithium batteries

LiNi0.7Co0.51Mn0.15O2 as a cathode material for lithium batteries was synthesized by mixing hydroxide co-precipitated precursors with 5% excess LiOH center dot H2O. Its structural and electrochemical properties were investigated using X-ray diffractometry, scanning electron microscopy, galvanostatic charge-discharge test, and electrochemical impedance spectroscopy. The results indicated that well-ordering layered LiNi0.7Co0.51Mn0.15O2 cathode materials were successfully prepared in air at 750, 800, and 850 degrees C with alpha-NaFeO2 typical crystal. The results of charge-discharge test demonstrated that the gradient cathode material sintered at 850 degrees C exhibited the best electrochemical performance with the initial discharge capacity of 164 mA h g(-1) at 0.2 C and lower electrochemical impedance. Nickel has low price. LiNiO2 cathode materials have high specific capacity, their theoretical capacity is 274 mA h g(-1) and with low self-discharge rate. So the Ni, Co, Mn ternary layer-structural compounds with high Ni content are showing to be promising cathode materials for lithium batteries. The techniques and research results in this paper are utilizable for the study of this kind of lithium battery materials. (C) 2012 Elsevier Ltd. All rights reserved.