Gleeble Testing to Assess Solid/Liquid Metal Embrittlement of Gun Steels by Copper

被引：10

作者：

Vigilante, G. N. ^{[1
]}

Bartolucci, S. ^{[1
]}

Izzo, J. ^{[1
]}

Witherell, M. ^{[1
]}

Smith, S. B. ^{[1
]}

机构：

[1] USA, Armament Res Dev & Engn Ctr, Benet Labs, Watervliet, NY 12189 USA

来源：

MATERIALS AND MANUFACTURING PROCESSES | 2012年 / 27卷 / 08期

关键词：

Artillery gun; Copper embrittlement; Coppering; Embrittlement; Environmental cracking; Gleeble; Gleeble testing; Gun steel; Liquid metal embrittlement; Solid metal embrittlement;

D O I：

10.1080/10426914.2011.648693

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Gleeble testing was performed to assess the solid/liquid metal embrittlement of gun steels by copper. An interior ballistics and finite element model provided the maximum bore temperatures in a 155 mm gun after aggressive firing. Specimens were manufactured out of three different steels. Testing was performed on bare steel as well as copper plated specimens at temperatures ranging from 868 degrees C to 1,100 degrees C. Additionally, notched and un-notched specimens were tested. After testing, metallography, scanning electron microscopy, and energy dispersive spectroscopy were performed. Embrittlement occurred in all copper plated steels tested at 1,100 degrees C. Below 1,100 degrees C, there was only slight evidence of embrittlement.

引用

页码：835 / 839

页数：5

共 50 条

[1] The influence of alloying on Zn liquid metal embrittlement in steels
Scheiber, D.
Prabitz, K.
Romaner, L.
Ecker, W.
ACTA MATERIALIA, 2020, 195 (195) : 750 - 760
[2] Liquid-metal embrittlement of copper wires
Brown, LE
ISTFA 2000: PROCEEDINGS OF THE 26TH INTERNATIONAL SYMPOSIUM FOR TESTING AND FAILURE ANALYSIS, 2000, : 449 - 455
[3] LIQUID-METAL EMBRITTLEMENT OF STEEL .1. A TESTING METHOD FOR LIQUID-METAL EMBRITTLEMENT
TAKEDA, T
AIHARA, S
YAMATO, K
GONDO, H
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1983, 23 (02) : B69 - B69
[4] Micromechanisms of liquid and solid metal induced embrittlement
Igoshev, V
ENVIRONMENTALLY INDUCED CRACKING OF METALS, PROCEEDINGS, 2000, : 103 - 110
[5] EMBRITTLEMENT OF SEVERAL STAINLESS-STEELS BY LIQUID COPPER AND LIQUID BRAZE ALLOYS
HEIPLE, C
BENNETT, W
RISING, T
MATERIALS SCIENCE AND ENGINEERING, 1982, 52 (03): : 277 - 289
[6] THE LIQUID-METAL EMBRITTLEMENT OF IRON AND FERRITIC STEELS IN SODIUM
HILDITCH, JP
HURLEY, JR
SKELDON, P
TICE, DR
CORROSION SCIENCE, 1995, 37 (03) : 445 - 454
[7] Crack path in liquid metal embrittlement: experiments with steels and modeling
Auger, T.
Hemery, S.
Bourcier, M.
Berdin, C.
Martin, M.
Robertson, I.
FRATTURA ED INTEGRITA STRUTTURALE, 2016, (35): : 250 - 259
[8] Penetration of liquid metals into solid metals and liquid metal embrittlement
Ina, K
Koizumi, H
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 387 : 390 - 394
[9] Liquid Metal Embrittlement of Galvanized Steels During Industrial Processing: A Review
Ling, Zhanxiang
Wang, Min
Kong, Liang
TRANSACTIONS ON INTELLIGENT WELDING MANUFACTURING, VOLUME I NO. 3 2017, 2018, I (03): : 25 - 42
[10] Liquid Metal Embrittlement of Galvanized TRIP Steels in Resistance Spot Welding
Jeon, Wook-Sang
Sharma, Ashutosh
Jung, Jae Pil
METALS, 2020, 10 (06) : 1 - 23

← 1 2 3 4 5 →