The Influence of Hydrogen on the Low Cycle Fatigue Behavior of Medium Strength 3.5NiCrMoV Steel Studied Using Notched Specimens

被引：9
|
作者：
Liu, Qian [1 ]
Atrens, Andrej [1 ]
机构：
[1] Univ Queensland, Mat Engn, St Lucia, Qld 4072, Australia
来源：
ADVANCED ENGINEERING MATERIALS | 2018年 / 20卷 / 02期
基金：
澳大利亚研究理事会;
关键词：
Hydrogen; Low cycle fatigue; Medium strength steel; Scanning electron microscopy; CRACK GROWTH; PLASTICITY; MECHANISM; FRACTURE; FAILURE;
D O I：
10.1002/adem.201700680
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The influence of hydrogen on low cycle fatigue (LCF) of 3.5NiCrMoV steel electrochemically hydrogen charged in the acidified pH 2 0.1M Na2SO4 solution is studied. In the presence of hydrogen, the fatigue life decreases significantly by approximate to 70 to approximate to 80% by: (i) the crack initiation period is decreased; and (ii) the crack growth rate is accelerated. SEM observation indicates that in the presence of hydrogen, the fracture surface shows flat transgranular fracture with vague striations and some intergranular fracture at lower stresses. The fatigue crack growth rate increases with increasing cyclic stress amplitude and with hydrogen fugacity. Once the fatigue crack reaches a critical length, the specimen becomes mechanical unstable and fracture due to ductile overload occurs. The hydrogen contribution to the final fracture process is not significant.
引用
收藏
页数：12
相关论文
共 50 条
  • [1] Reversible hydrogen trapping in a 3.5NiCrMoV medium strength steel
    Liu, Qian
    Atrens, Andrej
    CORROSION SCIENCE, 2015, 96 : 112 - 120
  • [2] The influence of hydrogen on 3.5NiCrMoV steel studied using the linearly increasing stress test
    Liu, Qian
    Irwanto, Bartolomeus
    Atrens, Andrej
    CORROSION SCIENCE, 2013, 67 : 193 - 203
  • [3] Fatigue propagation of short and long cracks in gaseous hydrogen environment in 3.5NiCrMoV steel
    Sarrazin-Baudoux, Christine
    Gardin, Catherine
    Chretien, Gaelle
    Pham, Tuan-Hiep
    Benoit, Guillaume
    Tran, Van-Xuan
    Petit, Jean
    ENGINEERING FAILURE ANALYSIS, 2016, 69 : 29 - 34
  • [4] THE INFLUENCE OF RELATIVE SLIP RANGE AND CONTACT MATERIAL ON THE FRETTING FATIGUE PROPERTIES OF 3.5NICRMOV ROTOR STEEL
    NIX, KJ
    LINDLEY, TC
    WEAR, 1988, 125 (1-2) : 147 - 162
  • [5] The effects of multiple overloads and absorbed hydrogen on the fatigue strength of notched steel specimens
    Kondo, Y.
    Yamanouchi, T.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2010, 33 (08) : 522 - 529
  • [6] Giga-cycle Fatigue Behavior of Notched Specimens for High Speed Steel
    Ebara, R.
    Nakamoto, K.
    Ogura, A.
    Ishihara, Y.
    Hamaya, S.
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS IX, 2011, 452-453 : 749 - +
  • [7] LOW-CYCLE FATIGUE BEHAVIOR OF NOTCHED AISI-304 STAINLESS-STEEL SPECIMENS
    BAYOUMI, MR
    ELLATIF, AKA
    JOURNAL OF MATERIALS SCIENCE, 1995, 30 (15) : 3944 - 3953
  • [8] Fatigue Strength Evaluation of Notched Ductile Steel Specimens Using Critical Distances
    Atzori, Bruno
    Ricotta, Mauro
    Campagnolo, Alberto
    Rigon, Daniele
    Meneghetti, Giovanni
    1ST VIRTUAL EUROPEAN CONFERENCE ON FRACTURE - VECF1, 2020, 28 : 1329 - 1339
  • [9] Low-cycle fatigue strength of notched low-carbon steel materials
    Department of Mechanical Engineering, Kinki University, 3-4-1 Kowakae, Higashi-Osaka-shi, Osaka, 577-8502, Japan
    Nihon Kikai Gakkai Ronbunshu A, 2006, 11 (1744-1750):
  • [10] The Influence of Heterogeneous Microstructure on Low-Cycle Fatigue Behavior in NiCrMoV Welded Joint
    Jiangkun Ma
    Jingchao Wang
    Haichao Cui
    Xinhua Tang
    Fenggui Lu
    Journal of Materials Engineering and Performance, 2022, 31 : 8226 - 8238
12345