InGaN Thin Films Grown by ENABLE and MBE Techniques on Silicon Substrates

The prospect of developing electronic and optoelectronic devices, including solar cells, that utilize the wide range of energy gaps of InGaN has led to a considerable research interest in the electronic and optical properties of InN and In-rich nitride alloys. Recently, significant progress has been achieved in the growth and doping of InGaN over the entire composition range. In this paper we present structural, optical, and electrical characterization results from InGaN films grown on Si (111) wafers. The films were grown over a large composition range by both molecular beam epitaxy (MBE) and the newly developed "energetic neutral atomic-beam lithography & epitaxy" (ENABLE) techniques. ENABLE utilizes a collimated beam of similar to 2 eV nitrogen atoms as the active species which are reacted with thermally evaporated Ga and In metals. The technique provides a larger N atom flux compared to MBE and reduces the need for high substrate temperatures, making isothermal growth over the entire InGaN alloy composition range possible. Electrical characteristics of the junctions between n- and p-type InGaN films and n- and p-type Si substrates were measured and compared with theoretical predictions based on the band edge alignment between those two materials. The predicted existence of a low resistance tunnel junction between p-type Si and n-type InGaN was experimentally confirmed.