Effects of Isothermal Aging on the Thermal Expansion of Several Sn-Based Lead-Free Solder Alloys

In this paper, effects of high-temperature aging on the thermal expansion behavior of several lead-free alloys SAC305, SAC387, Sn-3.5Ag, SnCu, SN100C (SnCu-Ni-Ge) and SnCu-0.01Ge have been explored. The coefficients of thermal expansion (CTEs) of the alloys have been experimentally determined over the temperature range 30-150 A degrees C after isothermal aging at 125 A degrees C for up to 30 days (720 h). The CTE values of SAC305, SAC387 and Sn-3.5Ag increase by 8-16% after 30 days of aging, while the CTE values of SnCu, SnCu-Ge and SN100C solders increase by only 3-6%. The CTE evolution of lead-free solders can be explained by microstructural changes observed during isothermal aging, which causes coarsening of various phases of the solder. As the phases coarsen, dislocation movement proceeds with a consequent increase in the average interparticle distance. The observation of CTE increases during isothermal aging suggests potential reliability problems for lead-free solder joints subjected to long-term aging exposures at high temperatures.