One-step hydrothermal preparation of bi- functional NiS2/reduced graphene oxide composite electrode material for dye-sensitized solar cells and supercapacitors

To screen out suitable electrode materials and overcome the shortcomings of the existed electrode materials for the application in dye-sensitized solar cells and supercapacitors, NiS2/reduced graphene oxide (NiS2/rGO) composite material was prepared by a simple onestep hydrothermal method in this paper and applied in the field of both dye-sensitized solar cells and supercapacitors as electrode material. In an electrolyte of 6 M KOH, the NiS2/rGO composite material with bilayer capacitance characteristics exhibited a high specific capacitance of 259.20 F g-1 at the current density of 0.6 A g-1, which was significantly higher than that of rGO (188.94 F g-1). Moreover, at a current density of 2 A g-1, the NiS2/rGO composite material had 92.85% capacitance retention after 2000 cycles. When applied as counter electrode material for the dye-sensitized solar cells, the NiS2/rGO composite material counter electrode exhibited a satisfactory photoelectric conversion efficiency (h) of 3.16% under standard simulated sunlight (AM 1.5 G), which was significantly higher than that of single rGO counter electrode (improved by 90.40%). The NiS2/rGO composite electrode material prepared by a simple one-step hydrothermal method is a potential bi-functional composite electrode materials for both dye-sensitized solar cells and supercapacitors.(c) 2023 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.