Performance of Particulate and Structured Pt/TiO2-Based Catalysts for the WGS Reaction under Realistic High- and Low-Temperature Shift Conditions

The water-gas shift (WGS) activity of Pt/TiO2-based powdered and structured catalysts was investigated using realistic feed compositions that are relevant to the high-temperature shift (HTS) and low-temperature shift (LTS) reaction conditions. The promotion of the TiO2 support with small amounts of alkali- or alkaline earth-metals resulted in the enhancement of the WGS activity of 0.5%Pt/TiO2(X) catalysts (X = Na, Cs, Ca, Sr). The use of bimetallic (Pt-M)/TiO2 catalysts (M = Ru, Cr, Fe, Cu) can also shift the CO conversion curve toward lower temperatures, but this is accompanied by the production of relatively large amounts of unwanted CH4 at temperatures above ca. 300 degrees C. Among the powdered catalysts investigated, Pt/TiO2(Ca) exhibited the best performance under both HTS and LTS conditions. Therefore, this material was selected for the preparation of structured catalysts in the form of pellets as well as ceramic and metallic catalyst monoliths. The 0.5%Pt/TiO2(Ca) pellet catalyst exhibited comparable activity with that of a commercial WGS pellet catalyst, and its performance was further improved when the Pt loading was increased to 1.0 wt.%. Among the structured catalysts investigated, the best results were obtained for the sample coated on the metallic monolith, which exhibited excellent WGS performance in the 300-350 degrees C temperature range. In conclusion, proper selection of the catalyst structure and reaction parameters can shift the CO conversion curves toward sufficiently low temperatures, rendering the Pt/TiO2(Ca) catalyst suitable for practical applications.