Stress corrosion crack initiation in filler metal 82 in oxygenated high-temperature water

被引：2
|
作者：
Supornpaibul, N. [1 ]
Duff, J. [1 ]
Burke, M. G. [1 ,2 ]
Wang, Y. [3 ]
Scenini, F. [1 ]
机构：
[1] Univ Manchester, Mat Performance Ctr, Sch Nat Sci, Dept Mat, Sackville St Campus, Manchester M13 9PL, England
[2] Oak Ridge Natl Lab, Oak Ridge, TN 37831 USA
[3] Hitachi Ltd, Prod Engn & MONOZUKURI, Prod Syst Res Dept, 7-1-1 Omika Cho, Hitachi, Ibaraki 3191292, Japan
来源：
CORROSION SCIENCE | 2023年 / 214卷
基金：
英国工程与自然科学研究理事会;
关键词：
Nickel; Welding; Alloy; 82; Stress corrosion; SSRT; Oxidation; PREFERENTIAL INTERGRANULAR OXIDATION; AUSTENITIC STAINLESS-STEEL; OXIDE-FILM FORMATION; ALLOY; 600; 288-DEGREES-C WATER; BOUNDARY MIGRATION; HYDROGENATED STEAM; NICKEL-ALLOYS; BEHAVIOR; MECHANISM;
D O I：
10.1016/j.corsci.2023.111008
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The Stress Corrosion Cracking (SCC) initiation in filler metal (FM) 82 was studied in oxygenated (O2) water at 288 degrees C. Post-test microstructural characterization revealed that cracked grain boundaries (GBs) always exhibited a porous oxide incursion. Some intergranular (IG) cracks exhibited an oxide along the crack walls, which appeared to form after the crack advanced. Furthermore, similar porous oxide incursions were observed at the GBs on the non-stressed FM 82 coupon after oxidizing for a similar duration. The formation of oxide incursions is discussed, and the evolution of crack initiation is proposed.
引用
收藏
页数：13
相关论文
共 50 条
  • [1] On the stress corrosion crack initiation behaviour of Alloy 800 in high-temperature hydrogenated water
    Zhang, Shihao
    Liu, Xiaoqiang
    Wang, Wei
    Han, En-Hou
    Kuang, Wenjun
    CORROSION SCIENCE, 2024, 238
  • [2] Investigation on the Stress Corrosion Crack Initiation and Propagation Behavior of Alloy 600 in High-Temperature Water
    Chen, Kai
    Wang, Jiamei
    Su, Haozhan
    Zhang, Lefu
    CORROSION, 2018, 74 (12) : 1395 - 1405
  • [3] Stress corrosion crack initiation in Alloy 690 in high temperature water
    Moss, Tyler
    Kuang, Wenjun
    Was, Gary S.
    CURRENT OPINION IN SOLID STATE & MATERIALS SCIENCE, 2018, 22 (01): : 16 - 25
  • [4] The effect of martensite on stress corrosion crack initiation of austenitic stainless steels in high-temperature hydrogenated water
    Chang, Litao
    Burke, M. Grace
    Mukahiwa, Kudzanai
    Duff, Jonathan
    Wang, YongLiang
    Scenini, Fabio
    CORROSION SCIENCE, 2021, 189
  • [5] Cold work and temperature dependence of stress corrosion crack growth of austenitic stainless steels in hydrogenated and oxygenated high-temperature water
    Arioka, K.
    Yamada, T.
    Terachi, T.
    Chiba, G.
    CORROSION, 2007, 63 (12) : 1114 - 1123
  • [6] Stress corrosion crack initiation testing with tapered specimens in high-temperature water - results of a collaborative research project
    Bosch, Rik-Wouter
    Ritter, Stefan
    Herbst, Matthias
    Kilian, Renate
    Burke, M. Grace
    Duff, Jonathan
    Scenini, Fabio
    Gu, Yuchen
    Dinu, Alice
    Ehrnsten, Ulla
    Toivonen, Aki
    Novotny, Radek
    Martin, Oliver
    Perosanz, Francisco-Javier
    Legat, Andraz
    Zajec, Bojan
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2021, 56 (02) : 103 - 118
  • [7] STRESS CRACK CORROSION-RESISTANCE OF HIGH ALLOYED MATERIALS IN HIGH-TEMPERATURE WATER
    WIELING, N
    STAHL UND EISEN, 1981, 101 (01): : 89 - 90
  • [8] Effects of acceleration factors on the probability distribution of stress-corrosion crack initiation life for alloys 600, 182, and 82 in high-temperature and high-purity water environments
    Akashi, M
    Nakayama, G
    PROCEEDINGS OF THE NINTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 1999, : 389 - 396
  • [9] THE STRAIN FOR STRESS-CORROSION CRACK INITIATION IN TYPE-316 STAINLESS-STEEL IN HIGH-TEMPERATURE WATER
    YANG, W
    CONGLETON, J
    KOHNEHCHARI, O
    SAJDL, P
    CORROSION SCIENCE, 1992, 33 (05) : 735 - +
  • [10] STRESS-CORROSION CRACKING OF SENSITIZED STAINLESS-STEEL IN OXYGENATED HIGH-TEMPERATURE WATER
    BERRY, WE
    WHITE, EL
    BOYD, WK
    CORROSION, 1973, 29 (12) : 451 - 469
12345