Zn Extraction from Zinc-Containing Sludge Using Ultrasonic Treatment Leaching with ChCl-MA DES

The recovery of zinc from metallurgical dust sludge is a crucial component of using solid waste as a resource in the metallurgical process, and deep eutectic solvent-ultrasonic synergistic enhanced leaching is an efficient method of doing so with excellent economic effects. The leaching rate of zinc is used as the value of response in this study, along with the four process conditions of leaching temperature, leaching time, liquid-solid ratio, and ultrasonic power. By building a regression model, the relationship between the various parameter components is investigated, and a strategy for optimization is then chosen and confirmed. The findings indicate that, for the parameters of temperature 40 & DEG;C, ultrasonic power 90 W, liquid-solid ratio 7:1 g/L, stirring speed 250 rpm, and leaching duration 80 min, the prediction value of the regression model of the zinc leaching rate is 98.47%. The average zinc leaching rate obtained by the 3 parallel verification experiments was 98.49%; the deviation from the regression model's predicted value was 0.02%. This demonstrated that the experimental results were consistent with those predicted by the regression model, the experimental results were reliable and trustworthy, and the optimization scheme was reasonable and accurate. Compared with the conventional leaching method (leaching rate: 91.61%), the method under ultrasound increased the zinc leaching rate by 6.88%.