Preparation of Densified Fine-Grain High-Frequency MnZn Ferrite Using the Cold Sintering Process

被引:7
|
作者
Ying, Yao [1 ,2 ]
Hu, Linghuo [1 ,2 ]
Li, Zhaocheng [1 ,2 ]
Zheng, Jingwu [1 ,2 ]
Yu, Jing [1 ,2 ]
Li, Wangchang [1 ,2 ]
Qiao, Liang [1 ,2 ]
Cai, Wei [1 ,2 ]
Li, Juan [1 ,2 ]
Bao, Daxin [3 ]
Che, Shenglei [1 ,2 ]
机构
[1] Zhejiang Univ Technol, Coll Mat Sci & Engn, Hangzhou 310014, Peoples R China
[2] Zhejiang Univ Technol, Res Ctr Magnet & Elect Mat, Hangzhou 310014, Peoples R China
[3] Hengdian Grp DMEGC Magnet Co Ltd, Dongyang 322118, Peoples R China
基金
中国国家自然科学基金;
关键词
MnZn ferrite; cold sintering process; power loss; high frequency; HIGH PERMEABILITY; MAGNETIC-PROPERTIES; POWER APPLICATIONS; ZN FERRITES; ADDITIVES; MICROSTRUCTURE; DENSIFICATION; REGION; IR;
D O I
10.3390/ma16093454
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The densified MnZn ferrite ceramics were prepared using the cold sintering process under pressure, with an acetate ethanol solution used as the transient solvent. The effects of the transient solvent, the pressure and annealing temperature on the density, and the micromorphology and magnetic properties of the sintered MnZn ferrites were studied. The densified MnZn ferrite was obtained using the cold sintering process and its relative density reached up to 85.4%. The transient solvent and high pressure are essential to the cold sintering process for MnZn ferrite. The annealing treatment is indispensable in obtaining the sample with the higher density. The relative density was further increased to 97.2% for the sample annealed at 950 ? for 6 h. The increase in the annealing temperature reduces the power loss at high frequencies.
引用
收藏
页数:12
相关论文
共 50 条
  • [21] Preparation of high density ZnO ceramics by the Cold Sintering Process
    Jiang, Xupeng
    Zhu, Guisheng
    Xu, Huarui
    Dong, Ling
    Song, Jinjie
    Zhang, Xiuyun
    Zhao, Yunyun
    Yan, Dongliang
    Yu, Aibing
    CERAMICS INTERNATIONAL, 2019, 45 (14) : 17382 - 17386
  • [22] Low-temperature annealing effect on plasma sprayed MnZn ferrite for planar transformers of high-frequency applications
    Yan, QY
    Gambino, RJ
    Sampath, S
    IEEE TRANSACTIONS ON MAGNETICS, 2003, 39 (05) : 3106 - 3108
  • [23] Plasma-sprayed MnZn ferrites with insulated fine grains and increased resistivity for high-frequency applications
    Yan, QY
    Gambino, RJ
    Sampath, S
    IEEE TRANSACTIONS ON MAGNETICS, 2004, 40 (05) : 3346 - 3351
  • [25] Effect of sintering process on microstructure and magnetic properties of high frequency power ferrite
    Sun Ke
    Lan Zhongwen
    Chen Shengming
    Sun Yueming
    Yu Zhong
    RARE METALS, 2006, 25 : 509 - 514
  • [26] PREPARATION OF HIGH-TEMPERATURE MATERIALS, USING METHOD OF DIRECT HIGH-FREQUENCY MELTING IN A COLD CONTAINER
    ALEKSANDROV, VI
    OSIKO, VV
    PROKHOROV, AM
    TATARINTSEV, VM
    USPEKHI KHIMII, 1978, 47 (03) : 385 - 427
  • [27] Coupling of MnZn-ferrite films onto electronic components by a novel solution process for high frequency applications
    Ailoor, Subramani K.
    Taniguchi, Takaaki
    Kondo, Koichi
    Tada, Masaru
    Nakagawa, Takashi
    Abe, Masanori
    Yoshimura, Masahiro
    Matsushita, Nobuhiro
    JOURNAL OF MATERIALS CHEMISTRY, 2009, 19 (31) : 5510 - 5517
  • [28] Preparation and properties of fine-grain (1-x)BiScO3-xPbTiO3 ceramics by two-step sintering
    Zou, Tingting
    Wang, Xiaohui
    Zhao, Wei
    Li, Longtu
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2008, 91 (01) : 121 - 126
  • [29] High-frequency noise suppression using ferrite-plated film
    Yoshida, Shigeyoshi
    Kondo, Koichi
    Ono, Hiroshi
    NEC TECHNICAL JOURNAL, 2006, 1 (05): : 77 - 81
  • [30] Dust grain dynamics due to nonuniform and nonstationary high-frequency radiations in cold magnetoplasmas
    Nekrasov, A. K.
    Feygin, F. Z.
    ANNALES GEOPHYSICAE, 2006, 24 (02) : 467 - 474