Effect of Annealing in Eutectic High-Entropy Alloy Superconductor NbScTiZr

We investigated the impact of annealing on the structural characteristics and superconducting critical temperature (T-c) of the eutectic high-entropy alloy (HEA) superconductor NbScTiZr. The HEA manifests an eutectic microstructure composed of body-centered cubic (bcc) and hexagonal close-packed phases. Both the lattice parameters of the bcc phase and grain size of the eutectic structure exhibited pronounced sensitivity to variations in annealing temperature. The observed dependence of the lattice parameter on annealing temperature supports the possibility that lattice strain occurs at lower annealing temperatures. The as-cast sample demonstrated superconductivity at T-c of 7.9 K, which increased to 9 K after annealing at 800 degrees C. However, when subjected to annealing at 1000 degrees C, T-c diminishes to 8.7 K. The annealing temperature dependence of T-c cannot be comprehensively elucidated based solely on the electronic density of states at the Fermi level. It is plausible that the lattice strain may influence the annealing temperature dependence of T-c. Our results for the critical current density J(c) reveal that the self-field J(c) of the as-cast NbScTiZr at 2 K exceeds 10(6) A/cm(2).