Effect of Carbon Nanoparticles on the Porous Texture of ?-Carrageenan-Based N-Doped Nanostructured Porous Carbons and Implications for Gas Phase Applications

S and N double-doped high surface area biomass-derived carbons were obtained from marine biomass-derived & iota;-carrageenan. Adding carbon nanoparticles (CNPs), namely graphene oxide (GO) or carbon nanotubes (CNTs), in the early stage of the synthesis leads to a modified porous texture and surface chemistry. The porous textures were characterized by N2 (-196.15 & DEG;C) and CO2 (0 & DEG;C) isotherms. The best GO- and CNT-added carbons had an apparent surface area of 1780 m2/g and 1170 m2/g, respectively, compared to 1070 m2/g for the CNP-free matrix. Analysis of the Raman spectra revealed that CNT was more efficient in introducing new defects than GO. Based on XPS, the carbon samples contain 2-4.5 at% nitrogen and 1.1 at% sulfur. The Dubinin-Radushkevich (DR) and Henry models were used to assess the strength of the interactions between various gases and the surface. The N2/H2 and CO2/CH4 selectivities were estimated with ideal adsorbed solution theory (IAST). While the CNPs, particularly GO, had a remarkable influence on the porous texture and affected the surface chemistry, their influence on the separation selectivity of these gases was more modest.