Indentation Size Effect on the Mechanical Properties of Supersonic Plasma Sprayed NiCr-Cr3C2 Coating

被引：0
|
作者：
Zhu Lina1
2 National Key Laboratory for Remanufacturing
机构：
来源：
稀有金属材料与工程 | 2012年 / 41卷 / S1期
关键词：
nanoindentation; mechanical property; indentation size effect;
D O I：
暂无
中图分类号：
TG174.44 [金属复层保护];
学科分类号：
080503 ;
摘要：
In this paper,NiCr-Cr3C2 coating was deposited onto AISI 1045 steel substrate by employing supersonic plasma spraying technique.The surface and cross-section morphologies of the NiCr-Cr3C2 coating were observed by SEM.The phase constituents of the coating were identified by XRD.The SEM images showed that the coating was very dense,and it had a low porosity structure.The XRD pattern implied that the coating was mainly composed of NiCr,Cr3C2 and Cr7C2.Nanoindentation tests were performed on the coating surface by a Nano indenter.The widely used Oliver-Pharr method was adopted to extract the mechanical properties of the coating.The hardness exhibited a strong peak-load-dependence,i.e.indentation size effect;the elastic modulus was not affected by indentation size effect.
引用
收藏
页码：296 / 298
页数：3
相关论文
共 10 条
  • [1] An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiment. Oliver WC, Pharr GM. Journal of Materials Research . 1992
  • [2] The role of microstructure in the high temperatureoxidation mechanism of Cr3C2–NiCr composite coatings. Matthews S,James B,Hyland M. Corrosion Science . 2009
  • [3] Suarez M,Bellayer S,Traisnel M et al. Surface and Coatings Technology . 2008
  • [4] Modification of composite hardness models to incorporate indentation size effects in thin films. Beegan D,Chowdhury S,Laugier M T. Thin Solid films . 2008
  • [5] Aguilar-Santillan J. Acta Materialia . 2008
  • [6] Zhu L,Xu B,Wang H et al. Journal of Materials Science . 2011
  • [7] Sun G,Zhang Y,Liu C et al. Materials and Design . 2010
  • [8] Culha O,Toparli M,Celik E et al. Surface&Coatings Technol- ogy . 2009
  • [9] Gong J H,Wu J J,Guan Z D. Materials Letters . 1999
  • [10] Indentation size effect in the nano and microhardness of fcc single crystal metals. Z. Zong,J. Lou,O.O. Adewoye,A.A. Elmustafa,F. Hammad,W.O. Soboyejo. Journal of Materials Science . 2006
1