Utilization of Coniferous and Deciduous Tree and Paper Ashes as Fillers of Rigid Polyurethane/Polyisocyanurate (PU/PIR) Foams

Five series of rigid polyurethane-polyisocyanurate (RPU/PIR) foams were obtained. They were modified by ashes from burning paper (P) and wood: conifers (pine-S, spruce-S') and deciduous trees (oak-D, birch-B). The ash was added to rigid polyurethane-polyisocyanurate foams (PU/PIR). In this way, five series of foams with different ash contents (from 1 to 9% wt.) were obtained: PP, PS, PD, PS', PB. The model foam (reference-W) was obtained without filler. The basic properties, physico-mechanical, and thermal properties of the ashes and obtained foams were examined. It was specified, among other things, the cellular structure by scanning electron microscopy (SEM), and changes in chemical structure by Fourier-transform infrared spectroscopy (FTIR) were compared. The obtained foams were also subjected to thermostating in a circulating air dryer in increased temperature (120 degrees C) for 48 h. Ash tests showed that their skeletal density is about 2.9 g/cm3, and the pH of their solutions ranges from 9 to 13. The varied color of the ashes affected the color of the foams. SEM-EDS tests showed the presence of magnesium, calcium, silicon, potassium, aluminum, phosphorus, sodium, and sulfur in the ashes. Foam tests showed that pine ash is the most beneficial for foams, because it increases their compressive strength three times compared to W foam and improves their thermal stability. All ashes cause the residue after combustion of the foams (retention) to increase and the range of combustion of the samples to decrease.