Physical Measurements on Iron-Aluminum Alloys with 10 to 50 at. % Al - VIII. Dependence of Shrinkage during Annealing of Quenched Iron Alloys with 40 to 50 at. % Al of the Heat Treatment Method.

被引：0

作者：

Koester, Werner

Goedecke, Tilo

机构：

来源：

Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques | 1984年 / 75卷 / 06期

关键词：

HEAT TREATMENT - Shrinking;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The shrinkage at the two annealing stages of quenched B2 Fe-Al alloys was measured on the 48 at. % Al alloy during constant rate heating and on the 46 at. % Al alloy during isothermal annealing. The amount depends on the heat treatment before quenching and on the way of testing the excess vacancy annihilation.

引用

页码：432 / 435

共 18 条

[1] Physical Measurements on Iron-Aluminum Alloys with 10 to 50% at. % Al.
Koester, Werner
Goedecke, Tilo
Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques, 1981, 72 (08): : 569 - 574
[2] Physical Measurements on Iron-aluminum Alloys with Al Content from 10 to 50 at. % - 3. The Expansion Coefficients of the Alloys with Al Content from 20 to 50 at. % ..
Koester, Werner
Goedecke, Tilo
Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques, 1981, 72 (10): : 707 - 711
[3] Physical Measurements on Iron-Aluminum Alloys with 10 to 50 at% Al.
Koester, Werner
Goedecke, Tilo
Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques, 1983, 74 (11): : 705 - 708
[4] PHYSICAL MEASUREMENTS ON IRON-ALUMINIUM ALLOYS BETWEEN 10 AND 50 AT-PERCENT-AL .8. ON THE DEPENDENCE OF SHRINKAGE DURING ANNEALING OF QUENCHED IRON-ALLOYS WITH 40 TO 50 AT-PERCENT-AL FROM THE HEAT-TREATMENT
KOSTER, W
GODECKE, T
ZEITSCHRIFT FUR METALLKUNDE, 1984, 75 (06): : 432 - 435
[5] PHYSICAL MEASUREMENTS OF IRON-ALUMINUM ALLOYS BETWEEN 10 AND 50 AT PERCENT AL .5. THE BEHAVIOR OF ALLOYS QUENCHED FROM 1100-DEGREE-C WITH 10 TO 26.5 AT PERCENT AL DURING TEMPERING
KOSTER, W
GODECKE, T
ZEITSCHRIFT FUR METALLKUNDE, 1982, 73 (08): : 502 - 510
[6] High Temperature Magnetic Measurements on Iron-Aluminum Alloys in the Range from 38 to 52 at. % Al.
Wachtel, Ernst
Bahle, Josef
Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques, 1987, 78 (03): : 229 - 232
[7] PHYSICAL MEASUREMENTS ON IRON-ALUMINUM ALLOYS BETWEEN 10 AND 50 AT-PERCENT AL .9. STATEMENTS ABOUT CONSTITUTION OF IRON-ALLOYS WITH 38 TO 50 AT-PERCENT AL BY MEANS OF SUSCEPTIBILITY MEASUREMENTS
KOSTER, W
WACHTEL, E
GODECKE, T
ZEITSCHRIFT FUR METALLKUNDE, 1985, 76 (05): : 382 - 387
[8] PHYSICAL MEASUREMENTS ON IRON-ALUMINUM ALLOYS BETWEEN 10-AT-PERCENT-AL AND 50-AT-PERCENT-AL .3. THE COEFFICIENTS OF EXPANSION OF THE ALLOYS BETWEEN 20-AT-PERCENT-AL AND 50-AT-PERCENT-AL
KOSTER, W
GODECKE, T
ZEITSCHRIFT FUR METALLKUNDE, 1981, 72 (10): : 707 - 711
[9] PHYSICAL MEASUREMENTS ON IRON-ALUMINUM-ALLOYS BETWEEN 10 AND 50 AT PERCENT AL .1. CONFIRMATION OF AND ADDITIONAL CONTRIBUTION TO THE IRON-ALUMINUM PHASE-DIAGRAM
KOSTER, W
GODECKE, T
ZEITSCHRIFT FUR METALLKUNDE, 1980, 71 (12): : 765 - 769
[10] PHYSICAL MEASUREMENTS ON IRON-ALUMINUM ALLOYS BETWEEN 10 AN 50 ATMOSPHERIC-PERCENT AL .10. EVALUATION OF SUSCEPTIBILITY VERSUS TEMPERATURE CURVES
KOSTER, W
WACHTEL, E
GODECKE, T
ZEITSCHRIFT FUR METALLKUNDE, 1985, 76 (10): : 676 - 683

← 1 2 →