Nitrogen Bubble Formation in Steel.

被引：0
|
作者：
Habel, L.
Steiger, J.
Zitter, Herbert
机构：
来源：
Giessereiforschung | 1972年 / 24卷 / 04期
关键词：
IRON AND ALLOYS - Solidification - STEEL CASTINGS;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The behavior of nitrogen during solidification of iron melts (high purity iron and 0. 1C - 0. 4Si - 0. 5Mn) is characterized by the maximum possible amount present after solidification (limiting saturation value, LSV) and the amount responsible for cavity formation (limiting porosity value, LPV). With increasing heat extraction rate (0 to 1000 cal/g. min), LSV increases from solubility in delta iron to solubility in molten iron, which suggests a diffusion controlled process at the solid/liquid interface. The LPV at intermediate heat extraction rates is 60 to 80 ppm nitrogen in Fe - 0. 4Si alloys and a multiple of this value in unalloyed steel castings.
引用
收藏
页码：141 / 146
相关论文
共 50 条
  • [1] ROLE OF NITROGEN IN THE EMBRITTLEMENT OF STEEL.
    Briant, C.L.
    Banerji, S.K.
    Ritter, A.M.
    1982, 13 (N 11): : 1939 - 1950
  • [2] CAUSES OF GAS BUBBLE FORMATION IN STEEL INGOTS CONTAINING NITROGEN
    IVANOV, BS
    KONDRATY.AI
    TOMILIN, IA
    LEVIN, FL
    MELKUMOV, IN
    RUSSIAN METALLURGY, 1972, (06): : 80 - 85
  • [3] Formation of basic slag in the manufacture of steel.
    Sillars, D
    TRANSACTIONS OF THE FARADAY SOCIETY, 1920, 16 (02): : 0315 - 0323
  • [4] Spheroidized Pearlite Formation in Hypereutectoid Steel.
    Tschiptschin, Andre Paulo
    Falleiros, Ivan Gilberto Sandoval
    Metalurgia ABM, 1984, 40 (316): : 145 - 150
  • [5] WEAR AND FRICTION OF NITROGEN ION IMPLANTED STEEL.
    Kirk, J.A.
    Egerton, G.W.
    Sartwell, B.D.
    1600, (105):
  • [6] Factors Influencing the Nitrogen Content in LD Steel.
    Kwitko, M.P.
    Jugow, P.I.
    Schachpasow, E.Ch.
    Krieger, Moskau W.
    Listhuber, F.E.
    Nakesch, J.
    Poferl, G.
    Truppe, M.
    Berg- und Huettenmaennische Monatshefte, 1982, 127 (01): : 6 - 14
  • [7] WEAR BEHAVIOUR OF NITROGEN IMPLANTED STAINLESS STEEL.
    Shrivastava, Sadhna
    Jain, Amitabh
    Sethuramiah, A.
    Vankar, V.D.
    Chopra, K.L.
    Nuclear Instruments and Methods in Physics Research, Section B: Beam Interactions with Materials and Atoms, 1986, B21 (2-4) : 591 - 594
  • [8] TEMPERATURE INFLUENCE DURING NITROGEN IMPLANTATION INTO STEEL.
    Moncoffre, N.
    Hollinger, G.
    Marest, G.
    Tousset, J.
    Jaffrezic, H.
    Nuclear Instruments and Methods in Physics Research, Section B: Beam Interactions with Materials and Atoms, 1985, B7-8 (pt 1) : 177 - 183
  • [9] Effect of Deoxidation on the Mechanism of Formation of Sulfides in Steel.
    Gromova, G.P.
    Vinograd, M.I.
    Kazichkina, G.M.
    1978, v (01): : 3 - 6
  • [10] FORMATION OF MnS-TYPE INCLUSION IN STEEL.
    Ito, Yoichi
    Masumitsu, Noriyuki
    Matsubara, Kaichi
    Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, 1980, 66 (06): : 647 - 656
12345