Contribution of the internal active three-phase zone of Ni-zirconia cermet anodes on the electrode performance of SOFCs

被引：0

作者：

Dept. of Biol. and Chem. Engineering, Gunma University, Tenjincho 1-5-1, Kiryu, Gunma 376, Japan ^{[1
]}

机构：

来源：

J Electrochem Soc | / 4卷 / 1290-1295期

关键词：

Anodes - Electrochemical electrodes - Fuel cells - Interfaces (materials) - Ionic conduction in solids - Microstructure - Reaction kinetics - Zirconia;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

An extension of the effective reaction zone of the Ni-zirconia cermet anode in a solid oxide fuel cell was investigated. The reaction zone, the active three-phase zone (ATZ), of the cermet electrode consists of the zone that is formed on the flat interface between the solid electrolyte and the cermet layer, ATZ2D, and another that extends three-dimensional into the cermet layer, ATZ3D, from the cermet/electrolyte interface. Anode performances of four types of cermet electrodes with zirconia powders of different ionic conductivities, but with a very similar microstructure, were compared, and the magnitude ratio of ATZ3D and ATZ2D was evaluated from the relationships between the performance and the ionic conductivity of zirconia in the cermet. For the anode of Ni-YSZ (yttria-stabilized zirconia, 8 mol % Y2O3) cermet on partially stabilized zirconia (3 mol % Y2O3) electrolyte, it was found that the contribution of ATZ3D was almost 2.5 times larger than that of ATZ2D at 1273 K, H2-H2O 2.4%.

引用