Effects of cathodic protection potential on corrosion fatigue crack growth for a duplex stainless steel in synthetic sea water

被引：0

作者：

Misawa, T. ^{[1
]}

机构：

[1] Muroran Technology Inst, Japan

来源：

Corrosion engineering | 1989年 / 38卷 / 05期

关键词：

Corrosion--Corrosion Fatigue;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The corrosion fatigue crack growth rate da/dN has been measured for α + γ duplex SUS 329J1 stainless steel in synthetic seawater with free corrosion and at various cathodic potentials for a frequency of 0.17 Hz. The effects of the cathodic potential on da/dN as a function of ΔK are discussed for values greater than 20 MPa&middotm 1/2 . With cathodic potentials of -0.40 to -0.80 V (Ag/AgCl), da/dN became much larger than on open circuit. Cathodic polarization potentials accelerated the growth rate considerably because of hydrogen embrittlement.

引用

页码：315 / 318

共 50 条

[1] Effect of cathodic protection potential on corrosion fatigue crack growth of a duplex stainless steel in synthetic sea water
Misawa, Toshihei, 1600, (38):
[2] Effects of protection potential on corrosion fatigue crack growth in high-tensile steel in synthetic sea water
Misawa, Toshihei
Ogasawara, Masaki
Moriyama, Etsuro
Sugawara, Hideo
Boshoku gijutsu, 1987, 36 (12): : 681 - 687
[3] CORROSION FATIGUE CRACK GROWTH OF A HIGH-TENSILE STRENGTH STEEL IN SYNTHETIC SEA WATER AND CATHODIC PROTECTION.
Komai, Kenjiro
Noguchi, Masatoshi
Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1986, 52 (480): : 1770 - 1777
[4] Corrosion fatigue crack growth inhibition of duplex stainless steel
Ahsan, M
Gasem, Z
DAMAGE AND FRACTURE MECHANICS VIII: COMPUTER AIDED ASSESSMENT AND CONTROL, 2004, 14 : 59 - 68
[5] EFFECT OF CATHODIC PROTECTION ON CORROSION FATIGUE BEHAVIOR OF CARBON STEEL IN SYNTHETIC SEA WATER
HUDGINS, CM
CASAD, BM
SCHROEDE.RL
PATTON, CC
JOURNAL OF PETROLEUM TECHNOLOGY, 1971, 23 (MAR): : 283 - &
[6] The effect of cathodic protection potential on corrosion fatigue crack growth rate of an offshore structural steel
Yu, J
Brook, R
Cole, I
Morabito, D
Demofonti, G
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1996, 19 (08) : 1019 - 1029
[7] The influence of nitrogen content on corrosion fatigue crack growth behavior of duplex stainless steel
Tseng, CM
Liou, HY
Tsai, WT
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 344 (1-2): : 190 - 200
[8] INFLUENCE OF ELECTROCHEMICAL POTENTIAL ON CRACK GROWTH RATEBY CORROSION FATIGUE IN SYNTHETIC SEA WATER.
SAITO, TETSUYA
UCHIYAMA, IKU
1982, V 22 (N 8): : 586 - 592
[9] CORROSION OF STAINLESS STEELS IN SEA WATER AND EFFECTIVENESS OF CATHODIC PROTECTION
LENNOX, TJ
GROOVER, RE
PETERSON, MH
MATERIALS RESEARCH AND STANDARDS, 1968, 8 (05): : 66 - &
[10] CORROSION FATIGUE CRACK GROWTH OF MEDIUM STRENGTH STEEL HT60 IN SYNTHETIC SEA WATER
GAO Hongbin
Acta Metallurgica Sinica(English Edition), 1992, (07) : 48 - 52

← 1 2 3 4 5 →