SPHEROIDIZATION OF MANGANESE SULFIDE INCLUSION DURING HEATING AND ITS EFFECT ON HYDROGEN INDUCED CRACKING IN ROLLED STEEL.

被引：1

作者：

Nishida, Minoru

Kato, Toshiyuki

Tanaka, Tomo

机构：

来源：

Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan | 1981年 / 67卷 / 09期

关键词：

D O I：

10.2355/tetsutohagane1955.67.9_1533

中图分类号：

学科分类号：

摘要：

Spheroidization behavior of manganese sulfide inclusions and associated decreases in hydrogen induced cracking were investigated in a hot rolled commercial API-X60 grade steel coil during various heat treatment. Cracking decreased as the temperature exceeded 1000 degree C.

引用

页码：1533 / 1541

共 50 条

[1] INITIAL COARSENING OF MANGANESE SULFIDE INCLUSIONS IN ROLLED STEEL DURING HOMOGENIZATION
MURTY, YV
MORRAL, JE
KATTAMIS, TZ
MEHRABIAN, R
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1975, 6 (11): : 2031 - 2035
[2] QUANTITATIVE MODELS OF HYDROGEN-INDUCED CRACKING IN HIGH STRENGTH STEEL.
van Leeuwen, H.P.
Reviews on Coatings and Corrosion (Corrosion Reviews), 1979, 4 (01): : 5 - 93
[3] STUDY ON HYDROGEN-INDUCED CRACKING AND EMBRITTLEMENT OF HIGH STRENGTH STEEL.
WEN-YUE, ZHANG
AKIO, HIROSE
1600,
[4] Effect of Carbon, Manganese, Silicon, and Aluminum Content on the Morphology of Sulfide Inclusions in Steel.
Se, Petr
Skala, Jiri
Sbornik Vedeckych Praci Vysoke Skoly Banske v Ostrave, Rada Hutnicka, 1977, 23 (01): : 191 - 204
[5] DYNAMIC OBSERVATION OF HYDROGEN-INDUCED CRACKING IN MEDIUM CARBON MARTENSITIC STEEL.
Tian, Yan
Nakagawa, Hiroji
Matsuda, Fukuhisa
Transactions of JWRI (Japanese Welding Research Institute), 1982, 11 (02): : 167 - 169
[6] EFFECT OF HYDROGEN PEROXIDE ON STRESS CORROSION CRACKING OF TYPE 304 STAINLESS STEEL.
Kikuchi, Eiji
Ohnaka, Noriyuki
Minato, Akira
Boshoku gijutsu, 1984, 33 (01): : 33 - 36
[7] EFFECT OF MICROSTRUCTURE ON HYDROGEN INDUCED CRACKING OF AN HSLA STEEL
STEVENS, MF
BERNSTEIN, IM
JOURNAL OF METALS, 1982, 34 (08): : 72 - 72
[8] Effect of hydrogen induced cracking on the integrity of steel components
Chattoraj, Indranil
Sadhana - Academy Proceedings in Engineering Sciences, 1995, 20 (pt 1):
[9] EFFECT OF GAS BLOWING METHOD IN TUNDISH ON INCLUSION REMOVAL FOR HYDROGEN-INDUCED CRACKING RESISTANCE STEEL
NAKAJIMA, K
KAWASAKI, M
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1994, 80 (08): : 611 - 616
[10] Effect of Carbon and Manganese on Low-Carbon Pipe Steel Hydrogen-Induced Cracking Resistance
A. A. Kholodnyi
Yu. I. Matrosov
M. Yu. Matrosov
S. V. Sosin
Metallurgist, 2016, 60 : 54 - 60

← 1 2 3 4 5 →