REVIEW OF THE CRYSTALLOGRAPHY OF STRESS CORROSION CRACKING.

被引：0
|
作者：
Meletis, E.I. [1 ]
Hochman, R.F. [1 ]
机构：
[1] IIT Research Inst, Chicago, IL, USA, IIT Research Inst, Chicago, IL, USA
来源：
Corrosion Science | 1986年 / 26卷 / 01期
关键词：
BRITTLE FAILURE - CORRODENTS - CRACK PROPAGATION - DUCTILITY - HYDROGEN-ASSISTED FRACTURE;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
(Edited Abstract)
引用
收藏
页码：63 / 90
相关论文
共 50 条
  • [1] CAUSTIC STRESS CORROSION CRACKING.
    Funk, C.W.
    Barton, G.B.
    Corrosion '77 $-$ Int Corros forum Devoted Exclusively to the Prot and Perform of Mater, 1977, : 1 - 54
  • [2] A REVIEW OF THE CRYSTALLOGRAPHY OF STRESS-CORROSION CRACKING
    MELETIS, EI
    HOCHMAN, RF
    CORROSION SCIENCE, 1986, 26 (01) : 63 - 90
  • [3] INTERGRANULAR MICROCHEMISTRY AND STRESS CORROSION CRACKING.
    Lea, C.
    Hondros, E.D.
    Proceedings of The Royal Society of London, Series A: Mathematical and Physical Sciences, 1981, 377 (1771) : 477 - 501
  • [4] Critical Potential of Stress Corrosion Cracking.
    Cihal, Vladimir
    Beran, Milan
    Kovar, Zdenek
    Kovove Materialy, 1979, 17 (02): : 239 - 249
  • [5] PREFACE TO THE PROBLEM OF STRESS CORROSION CRACKING.
    Brown, B.F.
    ASTM Special Technical Publication, 1972, : 3 - 15
  • [6] UNIFIED MECHANISM OF STRESS CORROSION AND CORROSION FATIGUE CRACKING.
    Jones, Denny A.
    Metallurgical transactions. A, Physical metallurgy and materials science, 1985, 16 A (06): : 1133 - 1141
  • [7] ELECTROCHEMICAL ASPECTS OF STRESS-CORROSION CRACKING.
    Fujii, C.T.
    Report of NRL Progress (Naval Research Laboratory, 1974, : 21 - 28
  • [8] FRONTIER AREAS IN THE ELECTROCHEMISTRY OF STRESS CORROSION CRACKING.
    Namboodhiri, T.K.G.
    Transactions of the SAEST (Society for Advancement of Electrochemical Science and Technology), 1984, 19 (03): : 197 - 199
  • [9] Cathodic Protection in Fatigue Stress Corrosion Cracking.
    Hirth, F.W.
    Speckhardt, H.
    Werkstoffe und Korrosion, 1973, 24 (09): : 774 - 781
  • [10] High Strength Steel Resistant to Stress Corrosion Cracking.
    Brandis, Helmut
    Engineer, Serosh
    Lennartz, Gustav
    Spyra, Wolfgang
    von den Steinen, Albert
    Thyssen Edelstahl Technische Berichte, 1979, 5 (03): : 186 - 193
12345