SOLUTION RATE OF ALLOYS IN CAST IRON.

被引：0
|
作者：
Cornell, Harry H. [1 ]
机构：
[1] Molycorp Inc, Pittsburgh, PA, USA, Molycorp Inc, Pittsburgh, PA, USA
来源：
Modern Casting | 1986年 / 76卷 / 03期
关键词：
CASTINGS - Physical Properties - METALS AND ALLOYS - Solubility;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
When purchasing alloys and in making alloy additions to molten metal, consideration should be given to the solution rate of the alloy. Basically, there are three methods by which alloys go into solution. When alloys are added to molten metal, a layer of metal solidifies on the surface of the cold alloy. It the melting point of the alloy is above that of the molten metal, it will not melt, but will dissolve into the bath after the shell has melted away. If the melting point of the alloy is below that of the molten metal, it will become liquid before the shell melts away and will mix into the bath when the shell melts. If the alloy has exothermic qualities and is reactive when added to the molten metal, the shell that is formed will be porous and the alloy will react quickly, melting the shell and dispersing throughout the molten metal.
引用
收藏
页码：40 / 41
相关论文
共 50 条
  • [1] MACHINING CAST IRON.
    Anon
    Casting Engineering, 1979, 11 (03): : 2 - 18
  • [2] Inoculation of Cast Iron.
    Henke, F.
    Giessereipraxis, 1980, (5-6): : 57 - 76
  • [3] Development of New Casting Alloys: Nodular Malleable Cast Iron.
    Fargues, Jacques
    Margerie, Jean Claude
    Fonderie, 1979, 34 (390): : 205 - 221
  • [4] Enamels for cast iron.
    Staley, HF
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1918, 1 (10) : 703 - 709
  • [5] MACHINING CAST IRON.
    Donaldson, E.G.
    Engineering (London), 1979, 219 (03):
  • [6] Inoculation of Cast Iron.
    Marincek, Borut
    Giesserei, 1975, 62 (26): : 692 - 694
  • [7] Synthetic cast iron.
    Mehrtens
    ZEITSCHRIFT DES VEREINES DEUTSCHER INGENIEURE, 1920, 64 : 309 - 310
  • [8] ENGINEERING CAST IRON.
    Moore, William H.
    Casting engineering & foundry world, 1985, 16 (04): : 26 - 31
  • [9] BEHAVIOR OF THE CERIUM AND SPHEROIDAL ALLOYS FOR SPHEROIDAL GRAPHITE CAST IRON.
    Kusakawa, Takaji
    Lin Hantong
    Xu, Xingcheng
    Report of the Castings Research Laboratory, Waseda University, 1985, (36): : 29 - 34
  • [10] The testing of cast iron.
    Moldenke, R
    JOURNAL OF THE FRANKLIN INSTITUTE, 1905, 159 : 405 - 422
12345