Assessment of the scatter of the time-to-failure during hydrogen-induced stress corrosion cracking testing

被引：0
|
作者：
Zitter, H. [1 ]
Kopetzky, H.G. [1 ]
God, Chr. [1 ]
机构：
[1] Montanuniv Leoben, Leoben, Austria
来源：
Werkstoffe und Korrosion | 1993年 / 44卷 / 06期
关键词：
15;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：249 / 255
相关论文
共 50 条
  • [1] ASSESSMENT OF THE SCATTER OF THE TIME-TO-FAILURE DURING HYDROGEN-INDUCED STRESS-CORROSION CRACKING TESTING
    ZITTER, H
    KOPETZKY, HG
    GOD, C
    WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1993, 44 (06): : 249 - 255
  • [2] Stress corrosion cracking and hydrogen-induced cracking of an alumina ceramic
    Shi, B
    Chu, WY
    Su, YJ
    Gao, KW
    Qiao, LJ
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2005, 88 (02) : 353 - 356
  • [3] HYDROGEN-INDUCED STRESS-CORROSION CRACKING ON A PIPELINE
    PUNTER, A
    FIKKERS, AT
    VANSTAEN, G
    MATERIALS PERFORMANCE, 1992, 31 (06) : 24 - 28
  • [4] Metallurgical factors in stress corrosion cracking (SCC) and hydrogen-induced cracking (HIC)
    Elboujdaini, M.
    Revie, R. W.
    JOURNAL OF SOLID STATE ELECTROCHEMISTRY, 2009, 13 (07) : 1091 - 1099
  • [5] Metallurgical factors in stress corrosion cracking (SCC) and hydrogen-induced cracking (HIC)
    M. Elboujdaini
    R. W. Revie
    Journal of Solid State Electrochemistry, 2009, 13 : 1091 - 1099
  • [6] Threshold Stress Intensity of Hydrogen-Induced Cracking and Stress Corrosion Cracking of High Strength Steel
    LI Hui-lu
    GAO Ke-wei
    QIAO Li-jie
    WANG Yan-bing
    CHU Wu-yang
    HUI Wei-jun
    DONG Han
    WENG Yu-qing
    Journal of Iron and Steel Research(International), 2001, 8 (02) : 42 - 46
  • [7] Threshold stress intensity of hydrogen-induced cracking and stress corrosion cracking of high strength steel
    Li, HL
    Gao, KW
    Qiao, LJ
    Wang, YB
    Chu, WY
    Hui, WJ
    Dong, H
    Weng, YQ
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2001, 8 (02) : 42 - 46
  • [8] HYDROGEN-INDUCED STRESS CORROSION CRACKING OF WELDED STRUCTURAL STEELS.
    Pircher, Hans
    Sussek, Gerd
    Stahl und Eisen, 1982, 102 (10): : 503 - 507
  • [9] Coupling aspects in the simulation of hydrogen-induced stress-corrosion cracking
    Brocks, Wolfgang
    Falkenberg, Rainer
    Scheider, Ingo
    IUTAM SYMPOSIUM ON LINKING SCALES IN COMPUTATIONS: FROM MICROSTRUCTURE TO MACRO-SCALE PROPERTIES, 2012, 3 : 11 - 24
  • [10] STRESS CORROSION AND HYDROGEN-INDUCED CRACKING BEHAVIOR IN AN Al ALLOY.
    Wang Yanbin
    Chu Wuyang
    Xiao Jimei
    Jinshu Xuebao/Acta Metallurgica Sinica, 1982, 18 (06): : 676 - 682
12345