Effect of ground layer on ultra long life fatigue behaviour in high carbon chromium bearing steel

被引：0
|
作者：
Lu, Liantao [1 ]
Shiozawa, Kazuaki [2 ]
Nishino, Seiichi [2 ]
机构：
[1] State Key Laboratory of Traction Power, Southwest Jiaotong University, Chengdu 610031, China
[2] Faculty of Engineering, Toyama University, Toyama 930-8555, Japan
来源：
Jixie Gongcheng Xuebao/Chinese Journal of Mechanical Engineering | 2007年 / 43卷 / 02期
关键词：
D O I：
10.3901/JME.2007.02.115
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：115 / 121
相关论文
共 50 条
  • [1] Fatigue fracture process of a high-carbon-chromium bearing steel in ultra-long life regime
    Lu, LT
    Shiozawa, K
    Morii, Y
    Nishino, S
    ACTA METALLURGICA SINICA, 2005, 41 (10) : 1066 - 1072
  • [2] Influence of deeply rolling process on ultra-long life fatigue behavior of high carbon-chromium bearing steel
    Lu Liantao
    Shiozawa Kazuaki
    Jiang Yan
    ACTA METALLURGICA SINICA, 2006, 42 (05) : 515 - 520
  • [3] S-N curve characteristics and subsurface crack initiation behaviour in ultra-long life fatigue of a high carbon-chromium bearing steel
    Shiozawa, K
    Lu, L
    Ishihara, S
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2001, 24 (12) : 781 - 790
  • [4] Effect of stress ratio on long life fatigue behavior of high carbon chromium bearing steel under axial loading
    Sakai, Tatsuo
    Sato, Yosuke
    Nagano, Yoshiyuki
    Takeda, Mitsuhiro
    Oguma, Noriyasu
    INTERNATIONAL JOURNAL OF FATIGUE, 2006, 28 (11) : 1547 - 1554
  • [5] Effect of hydrogen trapped by inclusions on ultra-long life fatigue failure of bearing steel
    Murakami, Y.
    Yokoyama, N.N.
    Takai, K.
    Zairyo/Journal of the Society of Materials Science, Japan, 2001, 50 (10) : 1068 - 1073
  • [6] Effect of inclusion type on the rotating bending fatigue properties of a high carbon chromium bearing steel
    Shi, Zhiyue
    Cao, Wenquan
    Shang, Chengjia
    Zhang, Xiaodan
    42ND RISO INTERNATIONAL SYMPOSIUM ON MATERIALS SCIENCE: MICROSTRUCTURAL VARIABILITY: PROCESSING, ANALYSIS, MECHANISMS AND PROPERTIES, 2022, 1249
  • [7] EFFECT OF COLD WORKING AND HIGH TEMPERATURE TREATMENT OF HIGH CARBON CHROMIUM BEARING STEEL ON ITS ROLLING CONTACT FATIGUE LIFE.
    Tsubota, Kazuichi
    Ohnishi, Kimio
    Takajo, Takashi
    Ishihara, Akiyoshi
    Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, 1984, 70 (08): : 854 - 860
  • [8] Very high-cycle fatigue behaviour of shot-peened high-carbon-chromium bearing steel
    Shiozawa, K
    Lu, L
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2002, 25 (8-9) : 813 - 822
  • [9] A novel oxide layer for achieving ultra-high rolling contact fatigue life of bearing steel
    Xia, Zhuofan
    Wu, Di
    Hao, Long
    Li, Yifeng
    Wang, Jianqiu
    Han, En-Hou
    TRIBOLOGY INTERNATIONAL, 2025, 207
  • [10] Fatigue behaviour of high carbon chromium steel bombarded with fine particles
    Ko, Haeng-Nam
    Itoga, Hisatake
    Hasegawa, Tatsuya
    Kagaya, Chuji
    Tokaji, Keiro
    Nakajima, Masaki
    Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 2002, 68 (03): : 484 - 490
12345