Influence of ruthenium ions on the precipitation of α-FeOOH, α-Fe2O3 and Fe3O4 in highly alkaline media

被引：0
|
作者：
Krehula, Stjepko [1 ]
Musić, Svetozar [1 ]
机构：
[1] Division of Materials Chemistry, Ruder Bošković Institute, P.O. Box 180, HR-10002 Zagreb, Croatia
来源：
Journal of Alloys and Compounds | 2006年 / 416卷 / 1-2期
关键词：
The influence of ruthenium ions on the precipitation of goethite (α-FeOOH); α-Fe2O3 and Fe3O4 in highly alkaline media was investigated by 57Fe Mössbauer and FT-IR spectroscopies; thermal field emission scanning electron microscope (FE SEM) and EDS. The presence of Ru-dopant strongly affected the precipitation of α-FeOOH at highly alkaline pH; i.e. the formation of α-Fe2O3 was also noticed. A decrease of hyperfine magnetic field (HMF) at RT from 35.1 T (undoped α-FeOOH) to 31.3 T for sample with [Ru]/([Ru] + [Fe]) = 0.0196 was assigned to the incorporation of ruthenium ions into the α-FeOOH structure. Mössbauer spectroscopy showed the formation of stoichiometric Fe3O4 for [Ru]/([Ru] + [Fe]) = 0.0291-0.0909. α-Fe2O3 and Fe3O4 did not show a tendency to the formation of solid solutions with ruthenium ions. FE SEM observations of the samples showed that reference α-FeOOH sample contained acicular particles of good uniformity; which increased the length up to ∼5 times with increase of concentration of ruthenium ions. On the other hand; large octahedral Fe3O4 crystals (particles) were associated with small particles of ruthenium (hydrous) oxide with a size in the range ∼100 nm or less. A possible catalytic action of ruthenium that created reduction conditions for Fe3+ ions and formation of Fe2+ ions for precipitation of Fe3O4 was discussed. © 2005 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：284 / 290
相关论文
共 50 条
  • [1] Influence of ruthenium ions on the precipitation of α-FeOOH, α-Fe2O3 and Fe3O4 in highly alkaline media
    Krehula, Stjepko
    Music, Svetozar
    JOURNAL OF ALLOYS AND COMPOUNDS, 2006, 416 (1-2) : 284 - 290
  • [2] Synthesis of Fe3O4, Fe2O3, Ag/Fe3O4 and Ag/Fe2O3 nanoparticles and their electrocatalytic properties
    Pan Lu
    Tang Jing
    Chen YongHong
    SCIENCE CHINA-CHEMISTRY, 2013, 56 (03) : 362 - 369
  • [3] Synthesis of Fe3O4,Fe2O3,Ag/Fe3O4 and Ag/Fe2O3 nanoparticles and their electrocatalytic properties
    PAN Lu
    TANG Jing
    CHEN YongHong
    Science China(Chemistry), 2013, 56 (03) : 362 - 369
  • [4] Synthesis of Fe3O4, Fe2O3, Ag/Fe3O4 and Ag/Fe2O3 nanoparticles and their electrocatalytic properties
    Lu Pan
    Jing Tang
    YongHong Chen
    Science China Chemistry, 2013, 56 : 362 - 369
  • [5] Influence of sulfate ions on conversion of Fe(OH)3 gel to β-FeOOH and α-Fe2O3
    Kanie, K
    Muramatsu, A
    Suzuki, S
    Waseda, Y
    MATERIALS TRANSACTIONS, 2004, 45 (03) : 968 - 971
  • [6] The influence of Cd-dopant on the properties of α-FeOOH and α-Fe2O3 particles precipitated in highly alkaline media
    Krehula, Stjepko
    Music, Svetozar
    JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 431 (1-2) : 56 - 64
  • [7] Thermodynamic Properties of α-Fe2O3 and Fe3O4 Nanoparticles
    Spencer, Elinor C.
    Ross, Nancy L.
    Olsen, Rebecca E.
    Huang, Baiyu
    Kolesnikov, Alexander I.
    Woodfield, Brian F.
    JOURNAL OF PHYSICAL CHEMISTRY C, 2015, 119 (17): : 9609 - 9616
  • [8] Interactions in γ-Fe2O3 and Fe3O4 nanoparticle systems
    Laha, S. S.
    Tackett, R. J.
    Lawes, G.
    PHYSICA B-CONDENSED MATTER, 2014, 448 : 69 - 72
  • [9] INTERACTION OF FE2O3, FE3O4 AND FEO WITH CHLORINE
    EVDOKIMOV, VI
    BABIEVSKAYA, IZ
    DROBOT, NF
    IMRE, B
    ILDIKO, P
    TAMASH, S
    ZHURNAL NEORGANICHESKOI KHIMII, 1985, 30 (06): : 1507 - 1512
  • [10] Kinetic Study on the Oxidation of Fe3O4 to γ-Fe2O3
    赵新宇
    李春忠
    郑柏存
    胡黎明
    华东理工大学学报(自然科学版), 1995, (05) : 561 - 566
12345