Hydration of Styrene-Acrylic Copolymer Modified Calcium Sulphoaluminate Clinker with Anhydrite

被引：0
|
作者：
Liu X. [2 ]
Wang R. [1 ,2 ]
机构：
[1] Key Laboratory of Advanced Civil Engineering Materials of Ministry of Education, Shanghai
[2] School of Materials Science and Engineering, Tongji University, Shanghai
来源：
Kuei Suan Jen Hsueh Pao/Journal of the Chinese Ceramic Society | 2022年 / 50卷 / 02期
关键词：
Anhydrite; Calcium sulphoaluminate; Hydration; Styrene-acrylic copolymer;
D O I：
10.14062/j.issn.0454-5648.20210575
中图分类号：
学科分类号：
摘要：
The effect of styrene acrylic (SA) copolymer on the early hydration of calcium sulphoaluminate-anhydrite composite was investigated by calorimetry, X-ray diffraction, thermogravimetic analysis, scanning electron microscopy, and inductively coupled plasma-optical emission spectroscopy. The results show that SA can delay the hydration process, reduce the content of ettringite (AFt), single sulfur calcium sulphoaluminate hydrate (AFm) and Al(OH)3 (AH3) in the accelerated hydration period, and promote the reaction of AH3 with anhydrite and calcium hydroxide to form AFt as well as the transformation of AFt to AFm in the late hydration period. Also, SA can rapidly reduce the surface tension of the pore solution, and the surface tension tends to be stable within the hydration reaction. SA can increase the pH value of the pore solution, increase the concentration of OH- and affect the concentration of Ca2+, SO42- and[Al(OH)4]- in the composite, and decrease the ion concentration and the precipitation rate of hydration products at the initial stage of hydration, thus delaying the hydration process and reducing the hydration products. © 2022, Editorial Department of Journal of the Chinese Ceramic Society. All right reserved.
引用
收藏
页码：354 / 363
页数：9
相关论文
共 30 条
  • [1] LU Lingchao, LI Yunchao, WANG Shoude, Et al., J Build Mater, 12, 6, pp. 631-634, (2009)
  • [2] WANG Peiming, LIU Engui, J Build Mater (in Chinese), 12, 3, pp. 254-258, (2009)
  • [3] HENG Yanyang, ZHAO Wenjie, Bull Chin Ceram Soc (in Chinese), 33, 6, pp. 1431-1438, (2014)
  • [4] ZHANG Hongbo, WANG Chong, LI Donglin, Et al., Bull Chin Ceram Soc (in Chinese), 33, 1, pp. 164-169, (2014)
  • [5] WANG R, WANG G., Influence and mechanism of zeolite on the setting and hardening process of styrene-acrylic ester/cement composite cementitious materials, Constr Build Mater, 125, pp. 757-765, (2016)
  • [6] WANG Chao, LIU Zhaoshuang, ZHAO Wenji, Bull Chin Ceram Soc (in Chinese), 36, 4, pp. 1254-1257, (2017)
  • [7] KONG Xiangming, LU Zichen, ZHANG Chaoyang, J Chin Ceram Soc, 45, 2, pp. 274-281, (2017)
  • [8] WANG M, WANG R, YAO H, Et al., Research on the mechanism of polymer latex modified cement, Constr Build Mater, 111, pp. 710-718, (2016)
  • [9] THOMAS P, YU J, PLANK J., Film Formation of a Non-ionic Ethylene-Vinyl Acetate Latex Dispersion in Cement Pore Solution, Proceedings of the 14th International Congress on Polymers in concrete, pp. 316-321, (2013)
  • [10] WU K, ZHANG D, SONG J., Properties of polymer-modified cement mortar using preenveloping method, Cem Concr Res, 32, 3, pp. 425-429, (2002)
123