Study on the performances of the Para-aramid fibrid

被引：0
|
作者：
Jiang, Ming [1 ]
Zhang, Mei-Yun [1 ]
Lu, Zhao-Qing [1 ]
Yang, Bin [1 ]
Liu, Jun-Hua [1 ]
机构：
[1] Shaanxi Province Key Laboratory of Papermaking Technology and Specialty Paper, Shaanxi University of Science and Technology, Xi'an 710021, China
来源：
Gongneng Cailiao/Journal of Functional Materials | 2014年 / 45卷 / 08期
关键词：
The surface morphology; chemical structure; degree of crystallinity and thermal properties of Para-aramid fibrid were studied by using SEM; AFM; FT-IR; XRD and TGA. This paper was used to offer an experimental foundation for promoting its extensive use as one kind of composite reinforced materials. Results indicated that Para-aramid fibrid was non-granular and small-sized; it had a fiber or film looking; roughness surface; supple shape. The fiber had a secondary amide structure; and its crystallinity was 28.55 percent. As a result; it contained amounts of amorphous compositions; and the crystalline size in fibers was tiny. The initial decomposition temperature of fiber was 490°C; TG10%; was; 550°C; thus demonstrated its stable molecular chain structure and excellent thermal properties;
D O I：
10.3969/j.issn.1001-9731.2014.08.016
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：08075 / 08078
相关论文
共 50 条
  • [1] Structure and properties of para-aramid fibrid and its para-phenylene tereph thalamide paper
    Lu, Zhaoqing
    Jiang, Ming
    Zhang, Meiyun
    Song, Shunxi
    Yang, Bin
    Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering, 2015, 31 (02): : 88 - 92
  • [2] The effect of phosphoric acid functionalization of para-aramid fiber on the mechanical property of para-aramid sheet
    Lu Z.
    Zhao Y.
    Su Z.
    Zhang M.
    Yang B.
    Su, Zhiping (18729586695@163.com), 2018, SAGE Publications Ltd (13) : 14 - 22
  • [3] The Effect of Phosphoric Acid Functionalization of Para-aramid Fiber on the Mechanical Property of Para-aramid Sheet
    Lu, Zhaoqing
    Zhao, Yongsheng
    Su, Zhiping
    Zhang, Meiyun
    Yang, Bin
    JOURNAL OF ENGINEERED FIBERS AND FABRICS, 2018, 13 (03): : 14 - 22
  • [4] Study on para-aramid paper reinforced by special resin
    State Key Lab. of Pulp and Paper Engineering, South China University of Technology, Guangzhou 510640, China
    Chung kuo Tsao Chih, 2008, 3 (22-24):
  • [5] Method for the synthesis of para-aramid nanofibers
    Yeager, Matthew P.
    Hoffman, Christopher M., Jr.
    Xia, Zhiyong
    Trexler, Morgana M.
    JOURNAL OF APPLIED POLYMER SCIENCE, 2016, 133 (42)
  • [6] Thermal Characteristics of Para-Aramid Fibres
    K. E. Perepelkin
    I. V. Andreeva
    E. A. Pakshver
    I. Yu. Morgoeva
    Fibre Chemistry, 2003, 35 : 265 - 269
  • [7] NEW CONCEPTS IN PARA-ARAMID FIBERS
    HEINRICH, K
    JUNG, H
    TEXTILE RESEARCH JOURNAL, 1992, 62 (12) : 771 - 775
  • [8] Microstructure organization in para-aramid fibers
    Davis, H
    Singletary, J
    Srinivasarao, M
    Knoff, W
    Ramasubramanian, MK
    TEXTILE RESEARCH JOURNAL, 2000, 70 (11) : 945 - 950
  • [9] Compounding with para-aramid fiber elastomers
    Tsimpris, C.W.
    Wartalski, J.
    Ferradino, A.G.
    Vanderbilt, R.T.
    Rubber World, 2001, 224 (01):
  • [10] Thermal characteristics of para-aramid fibres
    Perepelkin, KE
    Andreeva, IV
    Pakshver, EA
    Morgoeva, IY
    FIBRE CHEMISTRY, 2003, 35 (04) : 265 - 269
12345