Embrittlement of a Cr-Mo low-alloy steel due to low-temperature neutron irradiation

被引：0
|
作者：
Song, S.H. [1 ]
Weng, L.Q. [1 ]
机构：
[1] Department of Materials Science and Engineering, Shenzhen Graduate School, Harbin Institute of Technology, Shenzhen 518055, China
来源：
Acta Metallurgica Sinica (English Letters) | 2006年 / 19卷 / 01期
关键词：
Embrittlement - Mechanical properties - Neutron irradiation - Pressure vessels - Scanning electron microscopy - Yield stress;
D O I：
10.1016/S1006-7191(06)60019-7
中图分类号：
学科分类号：
摘要：
Embrittlement of a 2.25Cr1Mo steel stemming from neutron irradiation at 270°C is studied by virtue of small punch testing in conjunction with scanning electron microscopy. The ductile-brittle transition temperature determined by the small punch test is much lower than that determined by the standard Charpy test. There is some irradiation-induced embrittlement effect after the steel is irradiated for 46 days with a neutron dose rate of 1.05 × 10-8 dpa/s (displacement per atom per second).
引用
收藏
页码：20 / 26
相关论文
共 50 条
  • [1] EMBRITTLEMENT OF A Cr-Mo LOW-ALLOY STEEL DUE TO LOW-TEMPERATURE NEUTRON IRRADIATION
    S.H. Song and L.Q. Weng Department of Materials Science and Engineering
    ActaMetallurgicaSinica(EnglishLetters), 2006, (01) : 20 - 26
  • [2] Small punch test evaluation of neutron-irradiation-induced embrittlement of a Cr-Mo low-alloy steel
    Song, SH
    Faulkner, RG
    Flewitt, PEJ
    Marmy, P
    Weng, LQ
    MATERIALS CHARACTERIZATION, 2004, 53 (01) : 35 - 41
  • [3] COERCIVITY AND MICROSTRUCTURE OF LOW-ALLOY CR-MO STEEL
    STERNBERK, J
    KRATOCHVILOVA, E
    HREBIK, J
    GEMPERLE, A
    PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 1983, 79 (02): : 523 - 529
  • [4] Embrittlement of low-alloy structural steel by neutron irradiation
    A. V. Nikolaeva
    Yu. A. Nikolaev
    Yu. R. Kevorkyan
    A. M. Kryukov
    Yu. N. Korolev
    Atomic Energy, 2000, 88 : 281 - 287
  • [5] Embrittlement of low-alloy structural steel by neutron irradiation
    Nikolaeva, AV
    Nikolaev, YA
    Kevorkyan, YR
    Kryukov, AM
    Korolev, YN
    ATOMIC ENERGY, 2000, 88 (04) : 281 - 287
  • [6] Antimony-induced embrittlement in welding heat-affected zones in a Cr-Mo low-alloy steel
    Zheng, L.
    Song, S. -H.
    PHILOSOPHICAL MAGAZINE LETTERS, 2013, 93 (07) : 405 - 412
  • [7] ROLE OF IMPURITIES IN IRRADIATION EMBRITTLEMENT OF LOW-ALLOY STEEL
    NIKOLAEV, VA
    RYBIN, VV
    BADANIN, VI
    SOVIET ATOMIC ENERGY, 1979, 47 (01): : 523 - 527
  • [8] STRESS-CORROSION CRACKING AND CORROSION FATIGUE IN CR-MO LOW-ALLOY STEEL
    AIYAMA, S
    SHOJI, T
    TAKAHASHI, H
    SUZUKI, M
    CORROSION, 1978, 34 (10) : 325 - 331
  • [9] DEPENDENCE OF CHARACTERISTICS OF HYSTERESIS LOOPS ON DISLOCATION DENSITIES FOR LOW-ALLOY CR-MO STEEL
    STERNBERK, J
    KRATOCHVILOVA, E
    GEMPERLE, A
    FAJA, V
    WALDER, V
    CZECHOSLOVAK JOURNAL OF PHYSICS, 1985, 35 (11) : 1259 - +
  • [10] Embrittlement of Cr-Mo steels after low fluence irradiation in HEIR
    1600, Elsevier Science B.V., Amsterdam, Netherlands (218):
12345