Practice of reducing amendment rate of continuous casting slab for internal cracks

被引：0

作者：

He, Y.M. ^{[1
]}

Zhu, B. ^{[1
]}

Hu, B. ^{[1
]}

Zhou, R.Y. ^{[1
]}

Chen, W.M. ^{[1
]}

机构：

[1] Chongqing Iron and Steel Co., Ltd., Chongqing 400084, China

来源：

Kang T'ieh/Iron and Steel (Peking) | 2001年 / 36卷 / 02期

关键词：

Cracks - Management - Plate metal - Production control;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The common types of internal crack in continuous casting slab were described. The reasons and influencing factors of internal cracks in continuous casting slab were discussed. On the basis of practice of reducing the amendment rate of continuous casting slab for internal cracks at No. 7 Work of Chongqing Iron and Steel Co., all the efforts for reducing internal cracks in continuous casting slab were reviewed. It is shown that the management plays an important role in production.

引用

页码：23 / 25

共 50 条

[1] A Prediction Model for Internal Cracks during Slab Continuous Casting
Kong, Yiwen
Chen, Dengfu
Liu, Qiang
Long, Mujun
METALS, 2019, 9 (05)
[2] Prevention of corner cracks in slab continuous casting
Triolet, N.
Poelmans, K.
Mabelly, P.
Le Papillon, Y.
REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 2009, 106 (11): : 508 - 517
[3] Effects of continuous casting mould fluxes on reducing longitudinal and star cracks on a slab surface
WANG Qian 1
Journal of Chongqing University, 2004, (01) : 65 - 68
[4] INVESTIGATION OF INTERNAL CRACKS IN THE SLAB CONTINUOUS-CASTING OF STAINLESS AND HEAT-RESISTING STEELS
STEINMETZ, E
LINDENBERG, HU
LOH, J
STAHL UND EISEN, 1985, 105 (20): : 1049 - 1054
[5] FORMATION OF INTERNAL CRACKS ON CONTINUOUS-CASTING
FLENDER, R
WUNNENBERG, K
STAHL UND EISEN, 1982, 102 (23): : 1169 - 1176
[6] Application of a chamfer slab technology to reduce internal cracks of continuous casting bloom during soft reduction process
Zong, Nanfu
Zhang, Hui
Wang, Minglin
Lu, Zhifang
METALLURGICAL RESEARCH & TECHNOLOGY, 2019, 116 (06)
[7] Research on the formation mechanism of internal crack in the continuous casting slab
Chang, G.W.
Jin, G.C.
Chen, S.Y.
Yue, X.D.
Acta Metallurgica Sinica (English Letters), 2007, 20 (01) : 35 - 39
[8] RESEARCH ON THE FORMATION MECHANISM OF INTERNAL CRACK IN THE CONTINUOUS CASTING SLAB
G.W. Chang*
Acta Metallurgica Sinica(English Letters), 2007, (01) : 35 - 39
[9] Analysis of Internal Cracks in Continuous Casting Slabs with Soft Reduction
Wang, Bo
Zhang, Jiongming
Xiao, Chao
Wang, Shunxi
Song, Wei
HIGH TEMPERATURE MATERIALS AND PROCESSES, 2016, 35 (03) : 269 - 274
[10] Formation and Control of Transverse Corner Cracks in the Continuous Casting Slab of a Microalloyed Steel
Wang, Yadong
Ren, Qiang
Zhang, Lifeng
Yang, Xiaogang
Yang, Wen
Ren, Ying
Zhang, Haijie
STEEL RESEARCH INTERNATIONAL, 2021, 92 (06)

← 1 2 3 4 5 →