Study on microstructure control of copper-tin biphase interface in hot-dip tin-plated electronic copper strip

被引：1

作者：

Ouyang, Yulu ^{[1
]}

Liu, Yahui ^{[2
]}

Zhu, Qianqian ^{[1
]}

Zhang, Guoshang ^{[3
]}

Song, Kexing ^{[3
]}

Huang, Tao ^{[1
]}

Lu, Weiwei ^{[4
]}

Liu, Dong ^{[5
]}

Liu, Aikui ^{[5
]}

Wang, Binbin ^{[1
]}

Li, Qi ^{[1
]}

机构：

[1] Henan Univ Sci & Technol, Sch Mat Sci & Engn, Luoyang 471023, Peoples R China

[2] Henan Univ Sci & Technol, Sch Mechatron Engn, Luoyang 471023, Peoples R China

[3] Henan Acad Sci, Inst Mat, Zhengzhou 450002, Peoples R China

[4] Henan Univ Sci & Technol, Sch Chem & Chem Engn, Luoyang 471003, Peoples R China

[5] KMD Precise Copper Strip Henan Co Ltd, Xinxiang 453000, Peoples R China

来源：

JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T | 2024年 / 33卷

关键词：

Hot dip tin plating; Copper strip; Reflow welding; Copper-tin biphase interface; GROWTH-BEHAVIOR; SOLDER JOINTS; IN-SITU; CU; CU6SN5; SN; MECHANISMS; PHASE;

D O I：

10.1016/j.jmrt.2024.11.107

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In order to study the effect of reflow process parameters on the copper-tin biphase interface structure of hot dip tinned electronic copper strip, heat treatment of C14415 hot dip tinned electronic copper strip was carried out. Electron backscattering diffraction (EBSD) and transmission electron microscopy (TEM) were used to collect and analyze the microcosmic characteristics of the copper-tin biphase interface of hot dip tin-coated electronic copper strip after reflux. The results show that Cu6Sn5 and Cu3Sn are formed at the Cu-Sn biphase interface during reflow welding, and Cu6Sn5 is first formed at the Cu-Sn biphase interface, and Cu3Sn is gradually formed at the bottom of Cu6Sn5 when the Cu-Sn biphase interface forms a high temperature and stable environment. During the growth of Cu and Sn and its series of compounds, different reflow welding processes have no obvious effect on the distribution of interphase orientation difference. The competitive growth process of the multiphase interface during reflow welding was reconstructed through the distribution state of the multiphase interface under different reflow welding processes. The optimal process parameters of reflow welding were 290 degrees C-heat preservation for 3min-air cooling.

引用

页码：7169 / 7181

页数：13

共 50 条

[1] FRETTING CORROSION OF TIN-PLATED COPPER ALLOY
LEE, A
MAMRICK, MS
IEEE TRANSACTIONS ON COMPONENTS HYBRIDS AND MANUFACTURING TECHNOLOGY, 1987, 10 (01): : 63 - 67
[2] TRANSPORT OF MERCURY ALONG TIN-PLATED COPPER WIRES
OGSTON, WM
JOURNAL OF THE INSTITUTE OF METALS, 1972, 100 (DEC): : 384 - 384
[3] Accelerated testing of tin-plated copper alloy contacts
Malucci, RD
IEEE TRANSACTIONS ON COMPONENTS AND PACKAGING TECHNOLOGIES, 1999, 22 (01): : 53 - 60
[4] Accelerated testing of tin-plated copper alloy contacts
IEEE
不详
IEEE Trans. Compon. Packag. Technol., 1 (53-60):
[5] FRETTING CORROSION OF TIN-PLATED COPPER ALLOY.
Lee, Anthony
Mamrick, Michael S.
IEEE transactions on components, hybrids, and manufacturing technology, 1986, CHMT-10 (01): : 63 - 67
[6] FRETTING DAMAGE IN TIN-PLATED ALUMINUM AND COPPER CONNECTORS
BRAUNOVIC, M
IEEE TRANSACTIONS ON COMPONENTS HYBRIDS AND MANUFACTURING TECHNOLOGY, 1989, 12 (02): : 215 - 223
[7] Tin-plated Copper Alloys for Replacing Gold-plated Terminals
Ueda, Yutaro
Tsuru, Masahiro
Mitsui, Toshiyuki
R and D: Research and Development Kobe Steel Engineering Reports, 2024, 73 (02): : 140 - 145
[8] HOT-DIP TIN PLATING OF COPPER WIRES .2. SOLUTION OF COPPER WIRE IN TIN BATH - WETTING OF COPPER WIRE WITH TIN AND HEAT BALANCE OF WETTING
FIDOS, H
SCHREINE.H
ZEITSCHRIFT FUR METALLKUNDE, 1970, 61 (04): : 273 - &
[9] Effect of intermetallic phases on the performance of tin-plated copper connections and conductors
Braunovic, M
PROCEEDINGS OF THE FORTY-NINTH IEEE HOLM CONFERENCE ON ELECTRICAL CONTACTS, 2003, : 124 - 131
[10] ELECTROCHEMICAL STUDY OF COPPER-TIN AMALGAMS
KOVALEVA, LM
ZEBREVA, AI
ZHURNAL FIZICHESKOI KHIMII, 1964, 38 (05): : 1161 - 1165

← 1 2 3 4 5 →