Synthesis of multi-walled carbon nanotubes decorated with zno/ag na-noparticles by co-precipitation method

Background: This research indicated that such abstract are more informative and more readable, in field of preparation of nanocomposite materials. Aim: The purpose of this work represented by decoration of Carbon Nanotubes (CNTs) with nanopar-ticles using co-precipitation method and exhibit different physical properties from those of CNTs alone and its appropriate for this particular journal. Methods: Preparation MWCNTs surface by Ag/ZnO nanoparticles using two steps represented by acid treatment of MWCNTs in a mixture acid of sulfuric acid (95% H2SO4) and nitric acid (65% HNO3) at 3:1 ratio and second step represented by decoration of Ag/ZnO nanoparticles on F-MWCNTs using co-precipitation method to prepare ZnO/Ag nanoparticles decorated on F-MWCNTs as nanocomposite material. Results: The results of this work reveal the decoration of Ag-doped ZnO nanoparticles on the F-MWCNTs was achieved without any impurities as shown in XRD, Raman spectra and FTIR and FESEM observations reveal that Ag-doped ZnO nanoparticles have spherical morphologies and ad-hered on the functionalized MWCNTs, with diameters are about 22-30 nm. Also it is clear that there were no any other materials on the surface of F-MWCNTs except ZnO and Ag which verifies the results obtained from XRD and EDS analysis. Conclusion: In this article, Ag-doped ZnO nanoparticles have been successfully decorated on to modi-fied MWCNTs by an in-situ co-precipitation method. From XRD results, it can be seen that the (002) peak of MWCNTs slightly increased after the addition of Ag-doped ZnO nanoparticles. Raman spectra and FTIR analysis confirmed the formation of Zn-C or Zn-O-C bonds between acid-treated MWCNTs and Ag-doped zinc oxide. The FESEM and EDS analysis revealed that the decoration of Ag-doped ZnO nanoparticles on the F-MWCNTs was achieved without any impurities. Finally, the small sizes Ag-doped ZnO NPs deposited on F-MWCNTs make it very promising for biomedicine applications. © 2020 Bentham Science Publishers.