Hot corrosion and cyclic oxidation performance of a PtAl2-dispersed (Ni,Pt)Al coating prepared by low-activity high-temperature aluminizing

被引：0
|
作者：
Yang, Y.F. [1 ,2 ]
Ren, S.X. [1 ]
Ren, P. [1 ,2 ]
Wang, Q.W. [1 ]
Bao, Z.B. [2 ]
Li, W. [1 ]
Zhu, S.L. [2 ]
Wang, F.H. [3 ]
机构：
[1] Institute of Advanced Wear & Corrosion Resistant and Functional Material, Jinan University, West Huangpu Road 601#, Guangzhou,510632, China
[2] Laboratory of Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Wencui Road 62#, Shenyang,110016, China
[3] Corrosion and Protection Division, Shenyang National Laboratory for Materials Science, Northeastern University, Shenyang,110016, China
来源：
Journal of Alloys and Compounds | 2022年 / 911卷
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The dual phase PtAl2-dispersed (Ni,Pt)Al coating (DP coating) and single phase (Ni,Pt)Al coating (SP coating) have been prepared simultaneously with an intermediate Pt content at the surface before low-activity high-temperature aluminizing process. Hot corrosion and cyclic oxidation performance of these two Pt-modified coatings are investigated in comparison with unmodified NiAl coating (UM coating). The results show that DP coating displays better hot corrosion resistance than SP and UM coating due to its higher Al content and faster Al diffusion rate in PtAl2 phase. The cyclic oxidation resistance of DP coating is comparable to SP coating, while lighter rumpling is achieved at the surface of DP coating. This is because the volume change accompanied by phase transformation from ζ-PtAl2 to β-(Ni,Pt)Al in DP coating is less than that from β-(Ni,Pt)Al to γ’-Ni3Al in SP coating. Moreover, ζ-PtAl2 is superior to β-(Ni,Pt)Al in creep resistance, which also qualifies DP coating with less rumpling than SP coating with the same residual stress. © 2022 Elsevier B.V.
引用
收藏
相关论文
共 42 条
  • [1] Hot corrosion and cyclic oxidation performance of a PtAl2-dispersed (Ni,Pt)Al coating prepared by low-activity high-temperature aluminizing
    Yang, Y. F.
    Ren, S. X.
    Ren, P.
    Wang, Q. W.
    Bao, Z. B.
    Li, W.
    Zhu, S. L.
    Wang, F. H.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 911
  • [2] High-temperature oxidation and hot-corrosion behavior of a sputtered NiCrAlY coating with and without aluminizing
    Ren, Xin
    Wang, Fuhui
    SURFACE & COATINGS TECHNOLOGY, 2006, 201 (1-2): : 30 - 37
  • [3] Laser cladding Ni35Al2OFe intermetallic coating for resisting high-temperature oxidation and hot corrosion
    Xu, XY
    Zhong, ML
    Liu, WJ
    LASERS IN MATERIAL PROCESSING AND MANUFACTURING, 2002, 4915 : 227 - 233
  • [4] High-temperature Corrosion Resistance of Composite Coating Prepared by Micro-arc Oxidation Combined with Pack Cementation Aluminizing
    Huang Zu-jiang
    Jiang Zhi-qiu
    Dong Wan-bing
    Tong Qing
    Li Wei-zhou
    CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2018, 46 (01): : 44 - 52
  • [5] Cyclic oxidation and hot corrosion of Al2O3 or Y2O3-dispersed low-temperature chromizing coating
    Zhang, Hai-jun
    Sun, Jian-feng
    Zhou, Yue-bo
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2013, 23 (10) : 2923 - 2928
  • [6] Preparation and Enhanced Hot Corrosion Resistance of a Zr-Doped PtAl2+(Ni, Pt)Al Dual-Phase Coating
    Jiang Chengyang
    Yang Yingfei
    Zhang Zhengyi
    Bao Zebin
    Zhu Shenglong
    Wang Fuhui
    ACTA METALLURGICA SINICA, 2018, 54 (04) : 581 - 590
  • [7] High-temperature oxidation behaviour of refurbished (Ni,Pt)Al coating on Ni-based superalloy at 1100 °C
    Zhang, C. Y.
    Ma, Z.
    Dong, S. Z.
    Xu, M. M.
    Li, S.
    Zhang, C.
    Jiang, C. Y.
    Bao, Z. B.
    Zhu, S. L.
    Wang, F. H.
    CORROSION SCIENCE, 2021, 187
  • [8] High-temperature cyclic oxidation behavior of Al2O3-YAG composite coating prepared by EPD and microwave sintering
    Ren, Chao
    He, Yedong
    Wang, Deren
    APPLIED SURFACE SCIENCE, 2012, 258 (15) : 5739 - 5745
  • [9] The high-temperature oxidation behavior of hot-dipping Al-Si coating on low carbon steel
    Wang, Chaur-Jeng
    Chen, Shih-Ming
    SURFACE & COATINGS TECHNOLOGY, 2006, 200 (22-23): : 6601 - 6605
  • [10] High-temperature oxidation and hot corrosion behavior of the Inconel 738LC coating with and without Al2O3-CNTs
    Alsultani, Kadhim F.
    Majidi, Hassan Sh.
    Abdulameer, Sara
    Karkush, Mahdi
    JOURNAL OF THE MECHANICAL BEHAVIOR OF MATERIALS, 2023, 32 (01)
12345