Microstructure and mechanical properties of friction plug welding for friction stir welded aluminum alloy

被引：0

作者：

Liu K. ^{[1
]}

Sun Z. ^{[1
,2
]}

Yang X. ^{[1
]}

Du B. ^{[1
]}

Song J. ^{[2
]}

机构：

[1] Tianjin Key Laboratory of Advanced Joining Technology, School of Materials Science and Engineering, Tianjin University, Tianjin

[2] Tianjin Long March Rocket Manufacture Co., Ltd., Tianjin

来源：

Hanjie Xuebao/Transactions of the China Welding Institution | 2019年 / 40卷 / 06期

关键词：

Friction plug welding; Mechanical property; Microstructure; Welding process;

D O I：

10.12073/j.hjxb.2019400165

中图分类号：

学科分类号：

摘要：

Friction plug welding for AA2219-T87 friction stir welds were performed, the macro/micro structures, hardness distributions and tensile strength were observed and tested, and the tensile fracture was observed by scanning electron microscope. The main findings are as follows: With 7500rpm rotational speed and axial force 40 ~ 55 kN can obtain defect-free plug welded joint; The ultimate tensile strength (UTS) and elongation of FPW joint in perpendicular direction can reach 336 MPa and 8%, respectively, approximately 73. 9% and 66. 7% being equivalent to that of base metal; The weakest bonding regions are always produced at the bottom bonding interface between the BM and PM and how to control the connection quality of the bottom bonding interface should be the key factor affecting the tensile properties of the friction plug welding joint. © 2019, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved.

引用

页码：118 / 125

页数：7

共 10 条

[1] Wang D., Feng J., Guo D., Et al., Process of friction-stir welding high-strength aluminum alloy and mechanical properties of joint, China Welding, 13, 2, pp. 159-162, (2004)
[2] Xing L., Ke L., Liu G., Et al., Microstructure and performance analysis of friction stir welding of aluminum alloy LD10, Transactions of the China Welding Institution, 23, 6, pp. 55-58, (2002)
[3] Hartley P.J., McCool A., Friction plug weld repair for the space shuttle external tank, (2000)
[4] Fan P., Development of friction plug repair welding and key issues, Aerospace Manufacturing Technology, 2, 1, pp. 34-37, (2007)
[5] Zhao Y., Liu J., Zhu R., Et al., A new breakthrough of repair welding technology-friction plug welding, Welding & Joining, 9, pp. 16-21, (2009)
[6] Metz D.F., Weishaupt E.R., Barkey M.E., Et al., A microstructure and microhardness characterization of a friction plug weld in friction stir welded 2195 Al-Li, Journal of Engineering Materials and Technology, 134, 2, (2012)
[7] Metz D.F., Barkey M.E., Fatigue behavior of friction plug welds in 2195 Al-Li alloy, International Journal of Fatigue, 43, pp. 178-187, (2012)
[8] Luan G., Ji Y., Dong C., Et al., Microstructure of LY12 aluminum alloy welded joint of friction plug welding, Transactions of the China Welding Institution, 27, 10, pp. 1-3, (2006)
[9] Zhao Y., Liu J., Zhang J., Et al., Microstructure and mechanical properties of friction plug welded joint of 2014 aluminum alloy, Aeronautical Manufacturing Technology, 23, pp. 86-90, (2009)
[10] Wang G., Zhao Y., Kong D., Et al., Friction plug welding for welded joint defects of LD10 aluminum alloy, Welding & Joining, 6, pp. 38-42, (2010)

← 1 →