Wear behaviour analysis of thermo-mechanically processed AA7075 and AA7075/SiC/Graphite composite

The current work focuses on investigating the tribological performance of AA7075 alloy and AA7075 hybrid composite with SiC and graphite reinforcements of 2 and 0.5 wt percentages, respectively. The alloy and hybrid composite are fabricated through stir casting and thermo-mechanically processed through hot rolling routes. Dry sliding wear characterization has been carried out using a pin-on-disc wear testing setup for alloy and composite under various processing conditions using experiments designed according to Taguchi's L9 orthogonal array. The technique for order preference by similarity to ideal solution (TOPSIS) method has been adopted to achieve a single multi-response index (MRI) considering the minimization of multiple objective functions for specific wear rate (SWR) and coefficient of friction (COF). The analysis of variance (ANOVA) results of the MRI indicated that sample processing condition and load were the most significant parameters. The wear mechanism at different experimental conditions was studied using Scanning electron microscope (SEM) micrographs, energy dispersive spectroscopy analysis and 3D surface profile of wear track. The AA7075 composites are found to be comparatively good in all experimental conditions compared to the base alloy due to load-bearing SiC particles and solid lubricant graphite as reinforcing elements. The mechanically mixed layer (MML) formation in hybrid composites helped achieve good tribological properties. The AA7075 alloy and hybrid composites cross rolled at 350 degrees C yielded better results than other samples. The wear mechanism was abrasive and adhesive at low temperature and low load conditions in both alloy and hybrid composites. Whereas, at higher temperatures and high loads oxidative wear mechanism with delamination was prevalent. The transition of SWR from mild to severe value occurs at 250 degrees C in all experimental cases. The specific wear rate was improved by 85.64 % between worst and best conditions, i.e., annealed alloy and cross rolled composite.