Processing and Mechanics of Aromatic Vitrimeric Composites at Elevated Temperatures and Healing Performance

Carbon fiber reinforced polymer (CFRP) composites are renowned for their exceptional mechanical properties, with applications in industries such as automotive, aerospace, medical, civil, and beyond. Despite these merits, a significant challenge in CFRPs lies in their repairability and maintenance. This study, for the first time, delves into the processing and self-healing capability of aromatic thermosetting co-polyester vitrimer-based carbon fiber composites through mechanical testing. Vitrimers are an emerging class of thermosetting polymers, which, owing to their exchangeable covalent bonds, enable the re-formation of bonds across cracks. The specific vitrimer chosen for this study is an aromatic thermosetting co-polyester (ATSP). The mechanical properties of samples were analyzed initially through three-point bending (3PB) testing at room temperature before and after healing (by curing samples for 2 h at 280 degrees C). Samples were also 3PB tested at 100 degrees C to analyze their mechanical properties at an elevated temperature for comparison to the samples tested at room temperature. To investigate the fracture properties, optical microscopy images of samples were taken after 3PB tests, which were analyzed to observe crack initiation and crack growth behavior. Through load-displacement curves from double cantilever beam (DCB) mechanical testing, the Mode I crack initiation fracture toughness values of self-healed composites and control composites were calculated to evaluate healing efficiency in ATSP CFRP composites cured at 280 degrees C for 2 h. Scanning electron microscopy (SEM) showed a similar surface morphology of cracks before and after self-healing. Micro-computed tomography (CT) X-ray imaging confirmed that the healed samples closely resembled the as-fabricated ones, with the exception of some manufacturing voids, caused by outgassing in the initial healing cycle. This research demonstrated the ability for the in situ repair of ATSP CFRPs by restoring the fracture toughness to values comparable to the pristine composite (similar to 289 J/m(2)).