WO 3-x as an activation medium to prompt overall water splitting of NiFe-based electrocatalyst

The efficient oxygen evolution reaction (OER) is crucial for various electrochemical processes, especially for overall water splitting (OWS). In this study, we focus on the utilization of WO 3-x as an activation medium to enhance the OER performance of NiFe-based electrocatalysts. Firstly, we synthesize WO 3-x nanowires supported on nickel foam (NF) and then incorporate NiFe on WO 3-x nanowires by a simple hydrothermal method. The WO 3- x self -supported NiFe (Oxy)hydroxide (denoted as NiFe-W-O/NF) shows a three-dimensional stereostructure composed of ultrathin nanosheets (- 4.0 nm). This unique structure provides a large open surface for fuller diffusion of the electrolyte while exposing more active sites. The electronic interaction of tri-centers of NiFeW accelerates the surface reconstruction process of gamma -NiOOH and FeOOH, which are converted into the main active species in a short time. The electrochemical measurements confirm that the NiFe-W-O/NF has low OER overpotentials (233 mV at 10 mA cm -2 , 298 mV at 100 mA cm -2 ) and excellent stability (100 h in total) in 1 M KOH electrolyte. In addition, the NiFe-W-O/NF || NiFe-W-O/NF battery also exhibits a low cell voltage (1.52 V at 10 mA cm -2 ) with a stable lifetime (50 h) under alkaline conditions. These results highlight the great potential of NiFe-W-O/NF for practical applications.