Fatigue Life Assessment of Corroded Cables Based on Crack Propagation

被引：0
|
作者：
Wang T. [1 ,2 ]
Zhang J. [1 ]
Wang L. [1 ]
Ma Y. [1 ]
机构：
[1] School of Civil Engineering, Changsha University of Science & Technology, Changsha
[2] School of Civil Engineering, Central South University of Forestry & Technology, Changsha
来源：
Hunan Daxue Xuebao/Journal of Hunan University Natural Sciences | 2023年 / 50卷 / 01期
基金：
中国国家自然科学基金;
关键词：
bridge engineering; corrosion; crack propagation; fatigue life; fracture mechanics; parallel wire cable; random load;
D O I：
10.16339/j.cnki.hdxbzkb.2023009
中图分类号：
学科分类号：
摘要：
The parallel wire cable is regarded as a series-parallel model with multi-crack competition，and the initial crack size of corroded steel wire is determined by a pitting non-uniformity coefficient. Based on the probability distribution of the parameters of the fatigue crack growth rate model，the fatigue life of the cable under different wire breakage rates is calculated by using the Monte-Carlo simulation method of the whole process of fatigue failure，and the calculated results are verified by the test data. The results show that the wire-breaking rate of the cable conforms to the growth law of the power series with the increase in fatigue times. When the wire-breaking rate of cable reaches about 10%，the wire-breaking rate of cable increases rapidly and loses the ability to resist fatigue load. The more the series steel wire elements are divided in the fiber bundle model，the shorter the fatigue life of the cable，but this trend gradually stabilizes with the increase of the number of steel wire elements. The fatigue life of the corroded cable follows the Weibull distribution，and the pitting effect shortens the crack initiation life of the steel wire，resulting in a significant decrease in both the average fatigue life and variability of the cable with the increase of the degree of cor⁃ rosion，as well as a rapid deterioration of its anti-fatigue performance. The random load history is transformed into the repeated action of fatigue load spectrum block by the rain flow counting method. Based on the corrosion develop⁃ ment law of steel wire，the fatigue life of cables with different corrosion degrees is calculated，and the relationship model between cable corrosion degree and fatigue life degradation under random load is established. According to the P-dc-N curve，the fatigue reliability of corroded cables can be evaluated. It is necessary to accurately grasp the de⁃ fect or corrosion details of cable steel wire in the application. © 2023 Hunan University. All rights reserved.
引用
收藏
页码：90 / 99
页数：9
相关论文
共 26 条
  • [1] NAKAMURA S, SUZUMURA K., Experimental study on fatigue strength of corroded bridge wires［J］, Journal of Bridge Engineer⁃ ing, 18, 3, pp. 200-209, (2013)
  • [2] NAKAMURA S．, Experimental and analytical study on fatigue strength and stress concentration of corroded bridge wires［J］．Bridge Structures, 12, 1/2, pp. 21-31, (2016)
  • [3] LI X Z, Experimental study on fatigue performance of corroded high tensile steel wires of arch bridge hangers, China Civil Engineering Journal, 48, 11, pp. 68-76, (2015)
  • [4] STALLINGS J M, FRANK K H．, Cyclic fatigue life of cables［J］, Engineering Fracture Mechanics, 38, 4, pp. 341-347, (1991)
  • [5] STALLINGS J M, FRANK K H．, Stay-cable fatigue behavior［J］, Journal of Structural Engineering, 117, 3, pp. 936-950, (1991)
  • [6] CASTILLO E，, FERNANDEZ-CANTELI A．, A general regression model for lifetime evaluation and prediction［J］, International Journal of Fracture, 107, 2, pp. 117-137, (2001)
  • [7] LAN C M, Fatigue property assessment of parallel wire stay cable Ⅱ：fatigue life model for stay cable［J］, China Civil Engineering Journal, 50, 7, pp. 69-77, (2017)
  • [8] MA Y F，, CHEN Z C, Experimental and numerical study on fatigue crack growth of bridge suspender［J］, Journal of Disaster Prevention and Mitigation Engineering, 39, 1, pp. 23-30, (2019)
  • [9] Fatigue crack propagation characteristics of high-tensile steel wires for bridge cables, Fatigue & Fracture of Engineering Materials & Structures, 42, 1, pp. 256-266, (2019)
  • [10] ZHENG X L, LI X Z, Fatigue fracture surface analy⁃ sis and fatigue life estimation of corroded steel wires［J］, China Journal of Highway and Transport, 30, 4, pp. 79-86, (2017)
123