LOW-TEMPERATURE INTERNAL-FRICTION SPECTRUM OF CALCIUM-DOPED POLYCRYSTALLINE YBA2CU3O6+X

被引:6
|
作者
FEUSIER, G
MI, Y
SCHALLER, R
机构
[1] Ecole Polytechnique Fédérale de Lausanne, Dépt. de Physique, Inst. de Génie Atomique
关键词
D O I
10.1016/0038-1098(94)90552-5
中图分类号
O469 [凝聚态物理学];
学科分类号
070205 ;
摘要
Internal friction measurements (IF) in the kilohertz frequency range were performed on Ca doped polycrystalline YBa2Cu3O6+x. The samples were also characterized by DC electrical resistivity and X-ray measurements. The IF spectra obtained in the present investigation show an increase in the low temperature mechanical loss maxima at 95 K and 115 K with increasing Ca content. This could be interpreted as being due to an increase in the electrical charge density, the Y3+-ions being replaced by the lower valent Ca2+-ions, thus creating additional holes. Furthermore the fact that doping increases the electrical charge density is shown by a decrease in the electrical resistivity with increasing Ca content. Thus the low temperature IF peaks could be attributed to the hopping of electronic defects in the CuO2 planes and in the CuO chains, whose density increase with Ca content.
引用
收藏
页码:591 / 594
页数:4
相关论文
共 50 条
  • [1] LOW-TEMPERATURE INTERNAL-FRICTION SPECTRUM OF YBA2CU3OX
    MI, Y
    SCHALLER, R
    BERGER, H
    BENOIT, W
    SATHISH, S
    PHYSICA C, 1991, 172 (5-6): : 407 - 412
  • [2] LOW-TEMPERATURE INTERNAL-FRICTION SPECTRUM OF POLYCRYSTALLINE Y-BA-CU-O
    MI, Y
    SATHISH, S
    SCHALLER, R
    BENOIT, W
    BERGER, H
    JOURNAL OF THE LESS-COMMON METALS, 1990, 164 : 1420 - 1427
  • [3] LOW-TEMPERATURE OXYGEN ORDERING IN YBA2CU3O6+X
    ALIGIA, AA
    GARCES, J
    SOLID STATE COMMUNICATIONS, 1993, 87 (05) : 363 - 366
  • [4] Model for the low-temperature magnetic phases observed in doped YBa2Cu3O6+x
    Andersen, NH
    Uimin, G
    PHYSICAL REVIEW B, 1997, 56 (17): : 10840 - 10843
  • [5] INTERNAL-FRICTION MEASUREMENTS ON POLYCRYSTALLINE YBA2CU3O7-X
    WELLER, M
    JAEGER, H
    KAISER, G
    SCHULZE, K
    PHYSICA C, 1989, 162 : 953 - 954
  • [6] Low-temperature superstructures and incommensurate phases of YBa2Cu3O6+x
    Lapinskas, S
    Tornau, EE
    Rosengren, A
    Schleger, P
    PHYSICAL REVIEW B, 1995, 52 (21): : 15565 - 15569
  • [7] OXYGEN ORDERING IN YBA2CU3O6+X - LOW-TEMPERATURE EXPANSIONS
    OITMAA, J
    JIE, Y
    WILLE, LT
    JOURNAL OF PHYSICS-CONDENSED MATTER, 1993, 5 (25) : 4161 - 4170
  • [8] NO ANTIFERROMAGNETIC REORDERING AT LOW-TEMPERATURE IN PURE YBA2CU3O6+X
    CASALTA, H
    SCHLEGER, P
    BRECHT, E
    MONTFROOIJ, W
    ANDERSEN, NH
    LEBECH, B
    SCHMAHL, WW
    FUESS, H
    LIANG, RX
    HARDY, WN
    WOLF, T
    PHYSICA C, 1994, 235 : 1623 - 1624
  • [9] ACTIVATION PARAMETERS OF LOW-TEMPERATURE PEAK OF INTERNAL-FRICTION IN YBA2CU3O7-X CERAMICS
    NATSIK, VD
    PALVAL, PP
    ENGERT, J
    KAUFMANN, HJ
    FIZIKA NIZKIKH TEMPERATUR, 1989, 15 (08): : 836 - 840
  • [10] Low-temperature oxygen ordering and carrier concentration in YBa2Cu3O6+x
    Kuropyatnik, IN
    Lavrov, AN
    INORGANIC MATERIALS, 1998, 34 (11) : 1170 - 1176