EFFECTS OF HIGH-TEMPERATURE AUSTENITIZATION ON FRACTURE, FATIGUE AND STRESS-CORROSION CRACKING BEHAVIOR OF CAST AND FORGED HIGH-STRENGTH STEELS .1. MONOTONIC FRACTURE-BEHAVIOR

被引：3
|
作者：
CAO, WD [1 ]
LU, XP [1 ]
机构：
[1] TSING HUA UNIV,DEPT MECH ENGN,BEIJING,PEOPLES R CHINA
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1989年 / 110卷
关键词：
D O I：
10.1016/0921-5093(89)90166-4
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
引用
收藏
页码：151 / 164
页数：14
相关论文
共 50 条
  • [1] EFFECTS OF HIGH-TEMPERATURE AUSTENITIZATION ON FRACTURE, FATIGUE AND STRESS-CORROSION CRACKING BEHAVIOR OF CAST AND FORGED HIGH-STRENGTH STEELS .2. FATIGUE AND STRESS-CORROSION CRACKING BEHAVIOR
    CAO, WD
    LU, XP
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 110 : 165 - 174
  • [2] A COMPARATIVE-STUDY OF MONOTONIC FRACTURE, ENVIRONMENTALLY ASSISTED FRACTURE AND FATIGUE BEHAVIOR OF CAST AND FORGED HIGH-STRENGTH STEELS
    CAO, WD
    LU, XP
    LIU, JJ
    YANG, AD
    MATERIALS SCIENCE AND ENGINEERING, 1984, 63 (02): : 165 - 187
  • [3] MICROSTRUCTURAL EFFECTS ON THE STRESS-CORROSION CRACKING BEHAVIOR OF MEDIUM AND HIGH-STRENGTH STEELS
    KERR, R
    SOLANA, F
    BERNSTEIN, IM
    THOMPSON, AW
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1987, 18 (06): : 1011 - 1022
  • [4] EFFECTS OF MULTIFUNCTIONAL INHIBITORS ON CORROSION FATIGUE AND STRESS-CORROSION CRACKING OF HIGH-STRENGTH STEELS
    LYNCH, CT
    VAHLDIEK, FW
    BHANSALI, KJ
    SUMITT, R
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1977, 124 (08) : C283 - C284
  • [5] EFFECT OF PRESTRAIN AT ELEVATED-TEMPERATURE ON THE FRACTURE-BEHAVIOR OF HIGH-STRENGTH STEELS
    SATOH, K
    TOYODA, M
    MUTOH, Y
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1983, 105 (01): : 16 - 20
  • [6] A STUDY ON FRACTAL DIMENSION OF FRACTURE SURFACE CREATED BY STRESS-CORROSION CRACKING IN HIGH-STRENGTH STEELS
    LONG, QY
    CHEN, J
    CHEN, JZ
    MU, ZQ
    LUNG, CW
    SCRIPTA METALLURGICA ET MATERIALIA, 1992, 27 (10): : 1319 - 1324
  • [7] STRESS-CORROSION CRACKING CRITERIA FOR HIGH-STRENGTH STEELS
    KARLINSKI, W
    SZACHNOWSKI, W
    BRITISH CORROSION JOURNAL, 1995, 30 (02): : 116 - 118
  • [8] MICROSTRUCTURAL EFFECTS ON THE STRESS-CORROSION CRACKING SUSCEPTIBILITY OF HIGH-STRENGTH STEELS
    GUTIERREZSOLANA, F
    BERNSTEIN, IM
    THOMPSON, AW
    JOURNAL OF METALS, 1982, 34 (08): : 72 - 72
  • [9] CRACK BRANCHING BEHAVIOR IN STRESS-CORROSION CRACKING OF HIGH-STRENGTH STEEL
    HIROSE, Y
    MURA, T
    ENGINEERING FRACTURE MECHANICS, 1989, 34 (03) : 729 - 742
  • [10] INVESTIGATION OF MECHANISM OF STRESS-CORROSION CRACKING IN HIGH-STRENGTH STEELS
    MARICHEV, YA
    ROSENFELD, IL
    CORROSION, 1976, 32 (11) : 423 - 429
12345