Fracture toughness of thick plates of Ti-6Al-4V weldments

被引：0
|
作者：
Eizaguirre, I [1 ]
Santamaria, F [1 ]
Irisarri, AM [1 ]
Plaza, LM [1 ]
机构：
[1] INASMET, San Sebastian 20009, Spain
来源：
ECF 12: FRACTURE FROM DEFECTS, VOLS. I-III | 1998年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The fracture behaviour of thick plates of Ti-6Al-4V alloy joined by means of plasma are welding (PAW) and two different electron beam welding (EBW) procedures. In the whole temperature range PAW weld metal specimens exhibited higher toughness than base material. This behaviour has been attributed to the acicular microstructure of the weld metal compared to the equiaxic of parent alloy. EBW welded metals also showed higher toughness than base material although no so high as PAW ones. These results could be associated with the presence of a small volume fraction of brittle alpha prime martensite due to the higher cooling rate.
引用
收藏
页码：895 / 900
页数：6
相关论文
共 50 条
  • [41] Texture effects on shear response in Ti-6Al-4V plates
    Schoenfeld, SE
    Kad, B
    INTERNATIONAL JOURNAL OF PLASTICITY, 2002, 18 (04) : 461 - 486
  • [42] Effect of mean stress on fretting fatigue of Ti-6Al-4V on Ti-6Al-4V
    Lovrich, NR
    Neu, RW
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2006, 29 (01) : 41 - 55
  • [43] STRUCTURE AND PITTING CORROSION OF Ti-6Al-4V ALLOY AND Ti-6Al-4V WELDS
    Ferdinandov, Nikolay Vasilev
    Gospodinov, Danail Dimitrov
    Ilieva, Mariana Dimitrova
    Radev, Rossen Hristov
    PROCEEDINGS OF THE 7TH INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND SYSTEMS, 2018, : 325 - 330
  • [44] Fatigue Crack Growth Rate of Ti-6Al-4V Considering the Effects of Fracture Toughness and Crack Closure
    Zhang Junhong
    Yang Shuo
    Lin Jiewei
    CHINESE JOURNAL OF MECHANICAL ENGINEERING, 2015, 28 (02) : 409 - 415
  • [45] The use of compact specimens to determine fracture toughness anisotropy of Ti-6Al-4V additively manufactured for repair
    Ojo, Sammy A.
    Shrestha, Sulochana
    El Rassi, Joseph
    Panakarajupally, Ragav P.
    Manigandan, K.
    Morscher, Gregory N.
    Gyekenyesi, Andrew L.
    Scott-Emuakpor, Onome E.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2021, 823 (823):
  • [46] MICROSTRUCTURAL FACTOR WHICH CONTROLS THE TOUGHNESS IN TI-6AL-4V ALLOY
    NIINOMI, M
    KOBAYASHI, T
    SASAKI, N
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 25 (10) : B278 - B278
  • [47] STABLE CRACK-GROWTH DURING FRACTURE-TOUGHNESS TESTING IN TI-6AL-4V ALLOY
    KISHI, T
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1982, 46 (12) : 1120 - 1124
  • [48] Fatigue Crack Growth Rate of Ti-6Al-4V Considering the Effects of Fracture Toughness and Crack Closure
    ZHANG Junhong
    YANG Shuo
    LIN Jiewei
    Chinese Journal of Mechanical Engineering, 2015, (02) : 409 - 415
  • [49] Effects of notch width and loading rate on the dynamic mode II fracture toughness of Ti-6Al-4V
    Fan, Changzeng
    Xu, Zejian
    Han, Yang
    He, Xiaodong
    Tan, P. J.
    Liu, Yan
    Huang, Fenglei
    ENGINEERING FRACTURE MECHANICS, 2024, 304
  • [50] IMPROVEMENT OF TI-6AL-4V FRACTURE-TOUGHNESS BY SUB-TRANSUS HEAT-TREATMENT
    PLAZA, LM
    IRISARRI, AM
    GILNEGRETE, A
    SCRIPTA METALLURGICA ET MATERIALIA, 1990, 24 (09): : 1765 - 1769
12345