INFLUENCE OF IMPURITIES ON INTERGRANULAR CORROSION OF EXTRA HIGH PURITY AUSTENITIC STAINLESS STEELS

被引：0

作者：

Ioka, Ikuo ^{[1
]}

Suzuki, Jun ^{[1
]}

Motoka, Takafumi ^{[1
]}

Kiuchi, Kiyoshi ^{[1
]}

Nakayama, Junpei

机构：

[1] Japan Atom Energy Agcy, Tokai, Ibaraki, Japan

来源：

ICONE 17: PROCEEDINGS OF THE 17TH INTERNATIONAL CONFERENCE ON NUCLEAR ENGINEERING, VOL 1 | 2009年

关键词：

D O I：

暂无

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

An intergranular corrosion is observed in austenitic stainless steels exposed to high temperature, concentrated nitric acid (HNO(3)) solution with highly oxidizing ions. It is an Important degradation mechanism of austenitic stainless steels for use in a nuclear fuel reprocessing plant The intergranular corrosion is caused by the segregation of impurities to grain boundaries and the resultant formation of active sites. Extra High Purity (EHP (TM)) austenitic stainless steel was developed with conducting the new multiple refined inciting in order to suppress the total harmful impurities less than 100ppm. The intergranular corrosion behavior of EHP alloys with various impurities was examined in boiling HNO(3) solution with highly oxidizing ions to find a correlation between the intergranular corrosion and the impurities of EHP alloys A good correlation was confirmed between the degree of intergranular corrosion and the corrosion rate. The relationships between the corrosion rate and the impurities content of EHP alloys was determined using a multiple regression analysis The influence on corrosion rate became small in order of B, P, Si, C, S and Mn. It was important to control B in intergranular corrosion behavior of EHP alloys

引用

页码：563 / 567

页数：5

共 50 条

[41] INFLUENCE OF DIFFERENT METALLURGICAL FACTORS ON CONTINUOUS COOLING SENSITIZATION OF AUSTENITIC STAINLESS-STEELS DURING INTERGRANULAR CORROSION
BAROUX, B
MAITREPIERRE, P
MEMOIRES ET ETUDES SCIENTIFIQUES DE LA REVUE DE METALLURGIE, 1980, 77 (09): : 857 - 857
[42] AUSTENITIC STAINLESS STEELS WITH HIGH RESISTANCE TO STRESS CORROSION
FERREE, JA
JOURNAL OF METALS, 1968, 20 (08): : A25 - &
[43] Intergranular corrosion of welded joints of austenitic stainless steels studied by using an electrochemical minicell
Garcia, C.
de Tiedra, M. P.
Blanco, Y.
Martin, O.
Martin, F.
CORROSION SCIENCE, 2008, 50 (08) : 2390 - 2397
[44] BEHAVIOR OF AUSTENITIC STAINLESS-STEELS IN EVALUATION TESTS FOR DETECTION OF SUSCEPTIBILITY TO INTERGRANULAR CORROSION
BROWN, MH
CORROSION, 1974, 30 (01) : 1 - 12
[45] Influence of carbide precipitation and rolling direction on intergranular stress corrosion cracking of austenitic stainless steels in hydrogenated high-temperature water
Arioka, K.
Yamada, T.
Terachi, T.
Chiba, G.
CORROSION, 2006, 62 (07) : 568 - 575
[46] INTERGRANULAR CORROSION AND ITS PREVENTION OF BORON-ALLOYED AUSTENITIC STAINLESS-STEELS
TOMARI, H
FUJIWAR, K
UEDA, C
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 25 (04) : B132 - B132
[47] A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
Rahimi, S.
Marrow, T. J.
MATERIALS & DESIGN, 2020, 187
[48] Relationship between fitting and intergranular corrosion of nitrogen-bearing austenitic stainless steels
Mudali, UK
Dayal, RK
Gnanamoorthy, JB
Rodriguez, P
ISIJ INTERNATIONAL, 1996, 36 (07) : 799 - 806
[49] PITTING CORROSION AND INTERGRANULAR ATTACK OF AUSTENITIC CR-NI STAINLESS STEELS IN NASCN
IJZERMANS, AB
CORROSION SCIENCE, 1970, 10 (08) : 607 - +
[50] PITTING, CREVICE AND INTERGRANULAR CORROSION RESISTANCES OF TITANIUM MODIFIED AUSTENITIC STAINLESS STEELS.
Kamachi Mudali, U.
Dayal, R.K.
Seetharaman, V.
Gnanamoorthy, J.B.
Key Engineering Materials, 1987, 20-28 (pt 1-4)

← 1 2 3 4 5 →